毕业设计（论文）-生物医用镁合金的腐蚀与防护研究进展.docVIP

生物医用镁合金的腐蚀与防护研究进展 摘 要 由于具有优异的力学性能、生物相容性和可降解性，镁及其合金成为一种极具潜力的生物医用可降解金属植入材料，并且是目前该领域的研究热点。但由于镁及其合金具有较快的腐蚀速率，严重制约了其在临床上的应用。因此开发高强度、高韧性、高耐蚀且降解行为可控的高性能镁合金迫在眉睫。本文结合近五年积累的众位科研人员关于医用镁合金腐蚀与防护的研究资料，在此基础上综述了生物医用可降解镁合金的最新研究进展，分别详细介绍了镁及其合金作为生物医用材料的优势与不足、腐蚀机理，腐蚀的表征技术和腐蚀的防护技术的相关研究，并一定程度上分析了未来医用镁合金发展中需要解决的问题和未来发展方向。 关键词：镁合金；生物医用；腐蚀；防护 ABSTRACT Due to the excellent mechanical properties, biocompatibility and degradability, magnesium and its alloys become a potential biomedical degradable implant materials, which is the research focus in the field.However , the corrosion rate of magnesium and its alloys is faster,which severely restrict its clinical application.So the development of high strength, high toughness, high corrosion resistance and controllable degradation behavior of high performance magnesium alloys is imminent.Combining with nearly five years of accumulation of medical research data about corrosion and protection of the magnesium alloy which is made by爎esearchers v, on which this paper summarizes the latest research progress of magnesium and its alloys was introduced in detail, such as the advantages and disadvantages of biomedical materials, corrosion mechanism, characterization of corrosion and corrosion protection technology research, and to some extent, the analysis of the problems need to be solved in the development of future medical magnesium alloys and the future development direction. Key Words:magnesium alloys ; biomedical;corrosion ;protection 文献综述 作为材料的一个重要分支，生物医用材料 (Biomedicalmaterials)的发展和应用关系到人类的生命健康和社会文明的进步，正吸引着越来越多的关注。生物医用材料又称生物材料(Biomaterials)，它是指一类应用于人体的诊断和治疗，在生物体生理系统控制下部分或完全替代生物体某一复杂生理功能的物质。 如图1-1所示，目前生物医用材料已经广泛应用于人体的治疗和诊断:除脑组织和大部分内分泌系统之外，人体的绝大多数器官或组织都可以采用生物医用材料进行功能性替代[1]。 图1-1生物材料在人体中的应用 Fig.1-1 Application of biomaterials in humanbod 目前，镁合金作为医用植入材料，与现有已经进入临床使用的医用金属材料相比，具有以下的优势[2]: 良好的生物相容性；可在体内降解，无需二次手术；与人骨的密度、力学性能相近，避免了应力遮挡效应。不过镁合金较差的耐腐蚀性限制了它的应用和发展。并且迄今为止，将镁及镁合金应用于骨科医疗领域已经有很长历史。生物医用镁合金在最近几年更成为了研究热点。 1镁合金在生