激光熔覆Ni基微一纳米WC金属陶瓷涂层加工.docVIP

激光熔覆Ni基微一纳米WC金属陶瓷涂层 组织及干滑动磨损性能 匡建新 汪新衡 黄开有 （湖南工学院机械工程系材料系，湖南 衡阳 421002） 摘要：在45钢表面进行添加微—纳米WC颗粒的镍基自熔粉末激光熔覆处理，得到了不同Ni基WC合金涂层。对熔覆层进行了显微组织观察、硬度测定以及室温干摩擦磨损试验。结果表明，纳米晶WC的加入能改善涂层的耐磨性能，在本试验条件下，当纳米级WC和微米级WC各为15%时，涂层耐磨性能最佳，但纯纳米晶WC增强涂层耐磨性不佳，其主要磨损破坏方式随涂层中WC晶粒尺寸变化而有所变化。 关键词：激光熔覆；微一纳米WC；复合涂层；干滑动磨损 中图分类号：TG156. 99 文献标识码：A Microstructure and Wear Properties Under Dry Sliding of Micro-nano WC Composite Coatings by Laser Cladding Kuang Jian xin , Wang Xin heng , Huang Kai you （Dept.of Mechanical Engineening,Hunan institute of Technology, Hengyang Hunan 421002,China) Abstract: The laser cladding which self-fused Ni-based ceramic powder of micro-nano WC is used on the surface of 45 steel, Different Ni-based WC composite coatings be formed. Observing and analying the microstructure of cross section, determining the Microhardness, Checking the Wear Properties Under Dry Sliding and room temperature. The results show that the wear resistance of coats is improved for the affiliation of nanostructure-WC，Under the experimental conditions the best wear performance is from the coat with 15wt% nanostructure- WC:l5wt% microstructure-WC，but the wear resistance of the coat only with nanostructure-WC is not perfect. And the main wear mechanism of the coats could alter as the difference of WC crystal radius. Key words: laser cladding; micro-nano WC; composite coat; dry sliding wear 颗粒增强型复合材料近年来得到了迅速发展，利用激光熔覆技术制备金属基复合材料涂层，成为目前国内外研究的热点[1-3]。激光表面熔覆技术可以在低成本基材表面制备高性能涂层，尤其适用于一些在极端恶劣条件下服役的关键部件的表面强化。其中，激光熔覆Co包WC增强Ni基合金复合涂层显示出较多优点：较好的界面结合，高的硬度，优良的耐腐蚀性，与金属副对磨时较低的磨损量，相对低廉的成本[4-5]。但是，这些研究中所用WC粉末基本上为微米晶WC晶粒，极少见有采用纳米晶WC的报道，而在采用了纳米晶WC粉末的热喷涂和粉末烧结的报道中，多数认为材料的耐磨性得到改善[6-7]。为了了解纳米晶WC的加人对激光熔覆涂层组织结构和耐磨性能的影响，本文制备了微米和纳米Co- WC增强Ni基合金复合涂层，与硬质合金磨轮进行了室温干滑动磨损试验，研究了熔覆复合层组织形貌、显微硬度和干摩擦磨损性能，探讨了微一纳米WC复合涂层的磨损失效机制，为其推广应用提供一定的理论指导。 ﹡湖南省科技计划项目（项目编号：05JT1017)；湖南工学院重点科研项目（项目编号：HGZ0601） 作者简介：匡建新（1973，12—），男，湖南祁东人，副教授，硕士，主要从事金属材料及加工工艺的教学和科研工作，已发表论文2