对稀土改善铸钢中夹杂物的机理性研究.doc

对稀土改善铸钢中夹杂物的机理性研究 霍文霞，计云萍，金自力 （内蒙古科技大学 材料冶金学院，内蒙古 包头 014010） 摘要：针对不同稀土硅铁加入量的高锰铸钢与20MnCrNi2MoA铸钢， 在未腐蚀与腐蚀后的情况下采用SEM（scanning electron microscope）EDS（Energy Disperse Spectroscopy）TG142.72 文献标识码：A Effect of Metamorphism of The Cast Steel containing Different Content Rare Earth HUO Wen-xia, JI Yun-ping *, JIN Zi-li，REN Hui-ping (Inner Mongolia university of science and technology, Baotou 014010) study on high manganese steel casting and 20 MnCrNi2MoA cast steel with different content rare earth ferro silicon，In the case of not corrosion and corrosion， by he SEM (scanning electron microscope) and equipped with the EDS (Energy Disperse Spectroscopy) for inclusion morphology and Energy spectrum analysis. The results show that：rare earth join in cast steel, can effectively improve the inclusion of the form, distribution and its size, inclusions of cast steel play a good metamorphism. Cast steel；Rare Earth； inclusion；metamorphism 20MnCrNi2MoA铸钢，其目的在于分析稀土对铸钢的作用机理［5～8］，以便为稀土在铸钢中的应用提供理论依据并指导发展，降低成本，提高性能。 1 实验材料和方法 实验用钢由山西国营华晋冶金铸造厂提供的不同稀土硅铁加入量的高锰铸钢与20MnCrNi2MoA铸钢，其化学成分见表1.1，表1.2，表１1号试样稀土的收得率分别是La：0.0031%，Ce:0.032%,2是La：0.0048%，Ce:0.050%,2中2号试样的稀土收得率分别是La：0.0016%，Ce:0.013%，DK77系列电火花钼丝切割机，将铸钢试样分别切割成10mm×10mm×5mm的试样，经过磨样，抛光后采用QUANTA -400型环境扫描电子显微镜（SEM）EDS观察夹杂物的形态，5%的硝酸酒精腐蚀后再次采用在QUANTA -400型环境扫描电子显微镜（SEM）EDS观察夹杂物的形态与分布。 基金项目： 内蒙古自治区引导计划项目（编号 作者简介：霍文霞(1987-)，女，内蒙古乌海市人，硕士研究生；研究方向：稀土对高锰钢组织和性能的研究 *通讯联系人E-mail：renhuiping@ 表1 高锰铸钢的化学成分（%, 质量分数） 　　　　Table 1 Chemical composition of High Manganese Steel (%,mass fraction) 试 样号 C Si Mn P S Cr Ni Al Ti V 稀土硅铁加入量（kg/t） 1号 1.21 0.51 12.20 0.047 0.009 1.51 0.043 0.04 0.009 0.011 3 2号 1.11 0.73 12.56 0.054 0.007 1.44 0.05 0.063 0.01 0.012 5 20MnCrNi2MoA铸钢的化学成分（%, 质量分数） 　　　　　　Table 1 Chemical composition of 20MnCrNi2MoA (%,mass fraction) 试 样号 C Si Mn P S Cr Ni Al B 稀土硅铁加入量（kg/t） 1号 0.48 0.87 0.009 0.008 1.01 2.08 0.47 0.04 0.0032 0 2号 0.48 0.87 0.009 0.008 1.01 2.08 0.47 0.04 0.0032 2.14