XX大学本科毕业论文-理科.docVIP

摘要：本研究报道了一种用H2O2辅助水热法制备花状CuO纳米结构的方法，相比较于其他合成方法，该法具有方法简单、价格低廉、无毒等优点，并且CuO纳米结构的形状可通过H2O2的浓度来进行调整。详细的表征显示，制备出的CuO纳米结构是由许多纳米带组成，这些纳米带是从纳米结构的中心辐射出来的并形成直径为5–10 μm的花状。纳米带长2.5–5 μm，宽150–200 nm。 关键词：CuO，纳米结构，花状，辅助水热法  Abstract：Herein, we report a hydrogen peroxide-assisted hydrothermal route to synthesize flower-like CuO nanostructures. Compared with other synthesis, the method is simple, inexpensive and nontoxic. Moreover, the shape of CuO nanostructures can be tuned by simply adjusting the H2O2 concentration. The detailed characterizations revealed that the prepared CuOnanostructures are composed of numerous nanobelts radiating fromthe center of the nanostructure and forming a flower-like shape with a diameter of 5–10 μm. The nanobelts have the lengths of 2.5–5 μm and widths of 150–200 nm. The shape of CuO nanostructures can be tuned by varying the concentration of H2O2. Keywords：CuO, nanostructures, flower-like, assisted hydrothermal 目 录 1 前言 4 2 实验步骤 6 3 结果与讨论 6 3.1 产品的表征 6 3.2 H2O2浓度对CuO纳米结构的影响 8 3.3 花状CuO的形成机制 8 4 结论 10 参考文献 11 致谢 12 1 前言 CuO，作为一种重要的带有狭窄能带隙的p型半导体，已经被广泛应用于研究太阳能、电子、气体传感器、磁性、光开关、电池、多相催化等领域。迄今，已有多种方法用来合成CuO纳米结构。主要包括： （1）固相反应法[1] 固相反应法是将金属盐或金属氢氧化物按一定比例充分混合，研磨后进行煅烧，通过发生固相反应，直接制备超微粉，或者通过再次粉碎而得到超微粉。此法设备和工艺简单，反应条件容易控制，产率高，成本低，但产品粒度一般较大，且分布不均，易团聚。在固相合成过程中，反应速度是影响粒径大小的主要因素，主要体现在以下两个方面：一方面是研磨方式，采用事先将反应物进行充分研磨的方式，可增大反应物的比表面，加速反应物分子的扩散，从而加快反应进行。用这一研磨方式制得的粒径小于事先未将反应物研磨、直接混合研磨反应所得产物的粒径。另一方面，选择合适的反应体系是必要的，所选反应体系的反应速度快，单位时间成核数目多，抑制晶粒长大，反应所得产物的粒径较小。 （2）氧化法[2] 利用金属的氧化是制备过渡金属氧化物纳米材料的重要方法之一。利用这种方法制备CuO纳米材料，一般是以铜片(网、线)为基体，选择合适的氧化剂得到具有新颖形貌的CuO纳米结构。 （3）液相沉淀法[3] 沉淀法是合成纳米粒子最重要的化学方法，通常是在溶液状态下将不同化学成分的物质混合．在混合溶液中加入适当的沉淀剂制备纳米粒子的前驱体沉淀物，再将此沉淀物进行干燥或煅烧。从而制得相应的纳米粒子。例如，利用金属盐或氢氧化物的溶解度，调节溶液酸度、温度、溶剂，使其沉淀，然后对沉淀物洗涤、干燥、加热处理制成纳米粒子。溶液中的沉淀物可以通过过滤与溶液分离获得。 （4）水热合成法[4] 在特制的反应釜内，采用水溶液作为反应体系，通过高温高压将反应体系加热至临界温度，加速离子反应和促进水解反应，在水溶液或蒸汽流体中制备氧化物，再经过分离和热处理得到氧化物纳米粒子。一些常温常压下反应速度很慢的热力学反应，在水热条件下可以实现反应快速化。水热法的原料成本相对较低，所得纳米颗粒纯度高，分散性好，晶型好，且