《粉煤灰制备透水砖工艺优化毕业论文》.docVIP

毕 业 论 文题 目： 粉煤灰制备透水砖工艺优化学 院： 土木工程学院专 业： 无机非金属材料工程姓 名： 杨延丽学 号： 01指导老师： 王继娜完成时间： 2014年5月25号 助熔剂%，温度1050℃，保温时间min；（2）粉煤灰掺量45%，助熔剂%，温度1℃，保温时间min。 关键字：粉煤灰，透水砖，正交实验，抗压强度，透水系数AbstractThe Permeable brick,a new kind of building material with wonderful water permeability and water-retention,can well retard urban desert and heat island effect which come from the road surfacing of bound waterproof pavement. the thesis uses fay ash，which comes form Pingdingshan,as main raw material, the influence,which is caused by the dosage of fly ash,dosage of flux ,calcination temperature and soaking time,of the property of permeable brick by means of orthogonal experiment method ,in order to research the feasibility of making permeable brick with fly ash. the results show that the influence of various factors ,implying on the compressive strength is different,top to bottom are the dosage of fly ash calcination temperature,soaking time and the dosage of flux. two groups more reasonable technological parameters for this study are followed:(1)45% dosage of fly ash,4% dosage of flux,calcination temperature 1050℃,soaking time 60min.(2)45% dosage of fly ash,5% dosage of flux,calcination temperature1100℃,soaking time 60min. Key words:fly-ash, permeable brick, orthogonal, compressive strength, permeability coefficient目录 摘要 I Abstract II 目录 Ⅲ 1绪论 1 1.1课题的研究背景及意义 1 1.1.1课题的研究来源 1 1.1.2课题的研究目的与意义 1 1.2国内外研究现状 2 1.2.1国内研究现状 2 1.2.2国外研究现状 3 1.3研究内容 4 2实验材料与实验方法 5 2.1实验材料 5 2.2实验仪器 5 2.3实验方法 6 2.3.1实验方法的选择 6 2.3.2工艺流程 6 2.3.3实验方案 6 2.3.4试件的制备 7 3实验结果与分析 8 3.1实验结果 8 3.1.1 结果分析 8 4结论 13 5参考文献 21 6致谢 2111.1课题的研究背景及意义 近来国内建筑行业的快速发展，混凝土、水泥等建筑材料一路增长。根据调查，11年国内的水泥产量为20.85亿吨，在整个世界水泥行业内位列前茅。但是在水泥发展迅猛的同时造成了能源浪费和环境的严重污染。经长期调查研究，每生产1吨水泥需要1.7吨生料，其中包括耗约标准煤120千克，而污染更严重向大气排放约0.75-1吨CO2气体，1千克的SO2气体，大型规模的水泥厂每产生1吨水泥就会产生3-7千克的粉尘，小型的水泥厂则会更多［1］。生产水泥产生的CO2、SO2和粉尘严重污染环境和直接危害到人们的身体健康，同时消耗大量的煤能源。从能源消耗、环境和人民健康等问题考虑，寻找水泥的替代品必不可少。当然还有一个制约水泥快速发展的重要因素，那就是生产水泥的原料—石灰石和黏土，由于这两种原料属于不可再生资源国内的石灰岩数量有限，随着这