工程质量墙体裂缝控制细果则.docVIP

工程质量墙体裂缝控制细则 加气砌块强度低、吸水率高、收缩变形大，墙体抹灰易出现裂缝。这种质量通病给用户在后续装修、观感和心理上造成不良影响，涉及墙面裂缝的投诉越来越多，因此，对墙面裂缝控制要求日益严格，探索和采取一系列防治裂缝的措施已成为建筑行业各方主体共同关注的课题。文章分析了加气砌体墙面抹灰裂缝出现的原因并提出了一系列控制裂缝的措施。关键词：加气砌块 抹灰裂缝 控制措施Filling cracks in masonry walls plastering controlWanghan ， Huangsonglin/ China Construction Engineering Bureau Fifth Third Construction Company Limited Northwest, Xian in Shanxi,710075Abstract：Filling block low intensity, high water absorption, the deformation of contraction，Plastering cracks in the wall。This quality defects to the user in the follow-up decoration, the perception and psychological adverse impact，Cracks in the walls of the complaints involve more and more，Therefore, the cracks in the walls of increasingly stringent control requirements，Exploration and adopt a series of measures to crack the construction industry has become parties to the main topics of common concern。The article analyzed the masonry filling cracks in plaster walls and the reasons put forward a series of control measures to crack。Keywords：Canadian gas block??Plastering cracks Reason Control measures. 加气砌块强度等级低、吸水率高、收缩变形大，沿用传统的墙体砌筑与墙面抹灰工艺，会经常出现裂缝。这种质量通病，一直困扰着开发商和施工企业。涉及墙体裂缝乃至渗漏的投诉也越来越多，因此分析造成裂缝的原因，寻求控制裂缝发生的措施，已成为建筑行业各方主体共同关注的课题。现就笔者多年的现场施工实践谈几点加气砌体墙面抹灰裂缝控制的体会。 一、加气砌块性能 加气砌块是一种轻质墙体材料，具有良好的隔热性能，在我国夏热冬冷地区，160㎜厚以上的加气砌块墙体，不做保温隔热即可满足夏季隔热要求。加气砌块的原材料主要为水泥、石灰、砂、粉煤灰等，是水泥混凝土制品，水灰比大，胶结料多，易吸水膨胀，失水收缩，虽经蒸压，但收缩率目前受成本限制只能控制在0.04％～0.06％范围内，比烧结粘土砖大。 二、裂缝的原因分析 产生加气砌体墙面抹灰裂缝原因很多。例如，前道工序留下来的：砌体方面、设计构造方面、基础不均匀沉降引起连锁反应等原因。然而，最主要的比较常见的比较频发的还是温度变化、干缩变形、配合比不适合、抹灰工序操作不当等因素引起。根据成因最常见的裂缝可分为四类：温度裂缝、干缩裂缝、设计及构造缺陷造成的裂缝、施工质量造成的裂缝。1、温度裂缝 由于昼夜温差、室内外温差、季节温差所产生的温度变化，会引起材料的热胀冷缩。当约束条件下温度变形引起的温度应力足够大时，墙体就会产生温度裂缝，特别在围护结构的热桥处，温差应力影响较大，且出现频繁，如边框梁下沿墙体顶部的水平裂缝，门窗洞边的角裂缝，女儿墙根的水平裂缝，混凝土边框柱与内墙之间的竖向裂缝，建筑物顶层两端内外纵墙上的斜裂缝，其形态呈“八”字或“X”型。由于材料之间的线性膨胀系数不同，温差应力必然引起结构内外胀缩变形的不一致，也必然会将抹灰层拉裂。 有些围护结构的保温设计热阻过小，使墙体经常受到温度波侵入，反复变形；外保温没有赶在内抹灰之前，这也是产生温度裂缝的重要原因。 顶层温度影响最大，裂缝频繁。其作用机理如下：在阳光照射下(特别是南方地区夏季)屋面梁板及其他热桥处温度可高达60℃～70℃，而其下的