超支化聚酯改性的酚醛树脂固化性能大幅度提升 酚醛树脂(PF)与超支化聚酯(HBPE)共混体系中PF 的酚羟基与HBPE的端羟基发生了氢键作用, 并且共混体系显示出单一的玻璃化转变温度, 表明共混体系之间有较好的相容性; HBPE 的加入, 提高了PF 固化物的冲击强度和弯曲强度, 当HBPE 的含量为15 % 时, 冲击强度达到了最大值, 比原来未处理时提高了145 %, 增韧效果比较明显。威海晨源化工新材料有限公司整理自《超支化聚酯改性酚醛树脂的制备与固化性能研究》王松松1 , 周大鹏2* , 谷俐2 , 李坚1 , 俞立琼3 ( 1. 常州大学材料科学与工程学院, 江苏常州213164; 2. 嘉兴学院生物与化工学院, 浙江嘉兴314033; 3. 浙江嘉民塑胶有限公司, 浙江嘉兴314027) 中国塑料，2011，6（25）:34-37 Hyperbranched polyester modified phenolic resin curing performance improves significantly. In blend system of Phenolic resin (PF) and hyperbranched polyester (HBPE),PF phenolic hydroxyl group and HBPE terminal hydroxyl group occurs hydrogen bonding action, and the blends show single glass transition temperature, indicating better compatibility between the blends; adding HBPE can improve the impact strength of the cured PF and bending strength, when HBPE content is 15%, the impact strength is up to the maximum and improved over the original untreated by 145% , toughening effect is more obvious. Weihai CY Dendrimer Technology Co. Ltd forwards from Hyperbranched Polyester modified phenolic resins preparation and curing properties study Songsong Wang 1, Dapeng Zhou 2 *,Li GU 2,Jian Li1,LiQiong Yu 3 (1 School of Materials Science and Engineering of Changzhou , Changzhou, Jiangsu 213164; 2 School of Biological and Chemical Engineering of Jiaxing, Jiaxing 314033; 3. Zhe Jiang Jiamin Plastic Co., Ltd., Jiaxing, Zhejiang 314027) China plastics, 2011,6 (25) :34-37 ZYJ—437 电机试验记录 工程名称： 单元名称： 铭 牌 型 号 额定电压 接线方式 相 数 额定电流 出厂编号 功 率 额定转速 位 号 频 率 制造厂 绝缘试验直流电阻 被试部位 温度： 定子线圈 转子线圈 轴 承 正 常 直流电阻（Ω） 温度： ℃ 被试线圈 A B C 定子线圈 转子线圈 直流耐压及泄漏 试验电压 kV,等于电机额定电压的3倍。 泄漏电流 被试线圈 电压阶梯及1min泄漏电流（μA） 0.5倍 1倍 1.5倍 2.0倍 2.5倍 3倍 交流耐压：试验电压 kV，时间1分钟，情况 结论： 技术负责人： 试验班长： 试验人员： 年 月 日 ZYJ—437 电机试验记录 工程名称：采油三厂卫3#增注站改造工程 单元名称：电气部分 铭 牌 型 号 Y280M-4 额定电压 0.4kV 接线方式 Δ 相 数 三 额定电流 164.3A 出厂编号 420 功 率 90 kW