含针片状粗集料的堆砌性能及对混凝土的影响.docVIP

含针片状粗集料的堆砌性能及对混凝土的影响 摘要：针片状集料堆砌时符合双组分体系的理论堆砌规律。掺入适量针片状颗粒，可增大体系的堆砌度。针片状颗粒堆砌时有很大的机械咬合力，机械咬合力影响混凝土的密实成型， 进而影响混凝土的其他性能。 关键词：针片状 集料 堆砌 混凝土 The stacking properties and the influence to concrete of the aggregate containing elongated and flaky particles Abstract：When be piled up, elongated and flaky particles and non- elongated and flaky particles sysyem is in keeping with the theoretical stacking regularity of two-component system, and appropriate mixture of elongated and flaky particles and non- elongated and flaky particles will be denser. Elongated and flaky particles is closely related to more frictional resistance. More frictional resistance makes compaction of concrete difficult, and then proceed to affect other properties of concrete. Keywords：elongated and flaky particles, aggregate, stackable, concrete 《建筑用卵石、碎石》（GB/T14685-2001）规定的粗集料中针片状颗粒含量如下： 表1 粗集料中针片状颗粒含量 项 目 指 标 Ⅰ类 Ⅱ类 Ⅲ类 针片状颗粒（按质量计）/% 5 15 25 作者实测，粒径40㎜以下普通机制碎石中针片状颗粒含量大多在15 ~ 40%范围，针片状颗粒在粒径小的集料中的含量相对高些，超出表1范围的集料非常多。目前集料资源日益匮乏，充分认识针片状颗粒对集料和混凝土性能的影响，从而按材使用，具有显著的经济和社会意义。 1 双组分体系的理论堆砌问题 1.1双球堆砌体系的理论堆砌曲线［1］ B A 1.0 相对表观 体积 （1.0=100% 实体） C M 1.6 X=1 组成 X=0 Y=0 X+Y=1 Y=1 大球 小球 图1 双球堆砌体系的理论堆砌曲线 两种粒径球体的理论堆砌曲线见图1。图中参数及线段的含义： R—大球直径与小球直径之比； C—实验测定的大球理论密堆砌体积； M—实验测定的小球理论密堆砌体积； X，y—大球和小球的体积分数，总体积为1。 横坐标代表大、小球的组成，水平轴表示混合物的组成。 CA—小球加到大球中的浓缩曲线，曲线方程为V=Cx。 MB—大球加到小球中的浓缩曲线，曲线方程为V=x+My。 纵坐标代表相对表观体积（相对表观体积定义为体系的表观体积与真实体积的比值）。当体系固体物料的理论密堆砌度为1时，其相对表观体积为1；当固体物料的相对表观体积为1.6时，其理论密堆砌度为62.5%（单一粒径球体理论密堆砌度为62.5%［1］），即相对表观体积和理论密堆砌度互为倒数。