COATING DAMAGES AREAS ASSESSMENT REPORT 【DOC精选】.docVIP

Project: N407 Project Manager : Mr: Graham Location: COSCO qi dong shipyard Date: 2012-Aug-22 Position No 3 P Personnel attended during inspection: Shipyard coating inspector Shipyard project manager Shipyard coating supervisor Class representative Jotun representative Owner coating inspector The content of this report as following: 1 The survey assessment procedure 2 The condition of each part, bulkheads, underdeck, tanktop, The comparison of photos and standard( ASTM D610-1) 3 The general condition tank 4 The method of surface treatment and coating application procedure Survey procedure: 1 All hot work was completed, the tank was high pressure washed, and heat air dried before syrvey. 2 The survey and visual inspection results under the good illumination 3 The survey method according to 4 side PSPC agreement 4 Calculation is not include the butts and tight –seams coating damages 5 Calculation of the spot piece damages on bulkhead , underdeck , tanktop, each coating damages areas were calculated from similar figure area. 6 Confirm the percentage of damaged areas refer to ASTM D610-01 of annex 1,base on exact measure areas 7 Surface treatment method according to the PSPC requirement NO: CHART: Fore bulkhead Port bulkhead Tanktop Starboard bulkhead Support: L Burned: o Machinery: . Reinforcement: ｜ Pipe penetration: ◎ Contamination: ∷ Butts: ┅ After bulkhead Underdeck Project N407 Tank No 3P Total areas 2800 Damaged areas Fore bulkhead Port bulkhead Starboard bulkhead After bulkhead 1 stage support burned machinery reinforcement contaminated 2 stage support burned machinery reinforcement contaminated 3 stage support burned machinery reinforcement contaminated 4 stage support burned machinery reinforcement contaminated