预应力混凝土结构抗冻融耐久性的研究.docVIP

预应力混凝土结构抗冻融耐久性的研究 【摘要】随着预应力混凝土结构的广泛应用，其耐久性问题也越来越被人们所关注。由于预应力结构裂缝宽度很小，一般来说其耐久性要大大高于普通混凝土结构。但大量工程实践表明，预应力混凝土结构也普遍存在着耐久性问题，而冻融破坏是影响预应力混凝土耐久性的一大重要问题。近年来对于预应力混凝土抗冻融耐久性的研究中表明，氯盐溶液和应力作用对于预应力混凝土抗冻融耐久性有着重要的影响。氯盐溶液对于冻融破坏有着加速作用，应力作用对于抗冻融耐久性有可能是有利的，也有可能是不利的。 With the wide application of pre-stressed concrete structure, its durability problem has been concerned by more and more people. The prestressed structure crack width is very small, generally its durability is much higher than ordinary concrete structure. But a large number of engineering practice showed that, prestressed concrete structure durability problems also exists, and freeze-thaw damage is the effect of prestressed concrete durability is one of the most important issues. In recent years for prestressed concrete freeze thaw durability of results, chlorine salt solution and the effect of stress for prestressed concrete freeze thaw durability has important influence. Chlorine salt solution for freeze-thaw damage with acceleration, stress effects on freezing thawing durability may be beneficial, there may be adverse. 【关键词】预应力混凝土，耐久性，冻融破坏，除冰盐，应力，荷载 1.研究背景与意义 1.1 混凝土结构耐久性 混凝土结构的耐久性是指:结构在规定的使用年限内，在各种环境作用下，不需要额外的费用加固处理而保持其安全性、正常使用性和可接受的外观能力。影响混凝土结构耐久性的因素有内因和外因两个方面。内因包括混凝土的强度、渗透性、保护层厚度、裂缝、水泥品种、水泥标号及用量、外加剂、钢筋种类及构造等;外因包括环境温度、湿度、CO2含量、侵蚀性介质含量、应力水平、使用条件及防护措施等。在内外因素的共同作用下，混凝土结构主要会发生如下几种耐久性损伤[1]:1、钢筋腐蚀(主要源于氯盐侵蚀和混凝土碳化)，2、冻融破坏，3、碱一集料反应，4、应力腐蚀，5、化学介质侵蚀，6、疲劳，7、其他耐久性损伤，如高温损伤，生物腐蚀等。 耐久性支配着混凝土结构在整个服役过程中，结构耐久性不足所造成的后果非常严重。近四五十年来，国内外都有大量混凝土结构出现了因耐久性不足而过早失效甚至彻底损坏的现象。我国国内的大坝、道路、桥梁、海港和海上平台等混凝土结构也普遍存在耐久性问题。混凝土结构破坏面广，破坏速度快，沉重的重建与维修费用使混凝土结构的耐久性问题越来越受到关注和重视。 1.2 预应力混凝土结构耐久性 预应力混凝土结构耐久性与普通混凝土结构相比有明显的提高，预应力混凝土能避免或者延缓构件出现裂缝，并且能够限制裂缝的继续扩大。另外预应力混凝土构件内的预应力筋不容易被锈蚀，因此延长了构件的使用期限。但是由于预应力筋断面面积小而且长期处在高应力的状态，应力腐蚀及氢脆腐蚀的现象十分突出，预应力筋从开始腐蚀到失效历时很短，破坏形式表现为无任何先兆的脆性破坏。并且预应力技术要成功应用于工程中，需要经过多道工艺，如波纹管的制作、埋置、管道的灌浆、力筋的锚固及锚具的防腐处理等，任何一个环节的疏忽或质量的缺陷都有可能影响结构的耐久性[2]，因此预应力混凝土结构的耐久性比普通混凝土结构有更多和更高的要求。 世界范围内出现的一系列混凝土结构耐久性失效的事故中，预应力钢筋腐蚀引起的破坏占绝大多