B093 介孔二氧化钛的结构分析 1 於蕾 何明 陆小华 冯 新 （南京工业大学化学化工学院，南京，210009） 摘 要 研究了热处理过程中介孔氧化钛的结构及晶粒尺寸、比表面积间的相互关系，为纳米结构 材料的定量研究奠定了基础。借助圆柱通孔模型对介孔氧化钛结构分析时得到了较好的结果，说明 其高比表面积来自于纳米晶和孔结构两者共同作用的结果。并在晶粒尺寸、比表面积、孔容之间建 立了定量关系模型，不仅解释了其比表面积的变化规律，也使得预测孔结构数据成为了可能。 关键词 二氧化钛 介孔 比表面积 晶粒尺寸 中图分类号 TB383 STRUCTURE ANALYSIS OF TITANIA ON THE NANOMETER SCALE YU Lei, HE Ming, LU Xiao-Hua, FENG Xin (Institute of Chemistry and Chemical Engineering, Nanjing, 210009) Abstract The structure and relationship between crystallite size and specific surface area of mesoporous titania obtained by different temperatures were studied, which made a foundation for the quantitative study of the nanometer scaled material. With the application of the cylinder skeleton model, the structure of mesoporous titania was analysed, and preferable results were gained. It is concluded that the high specific area of mesoporous titania is the synergism effect of nanocrystalline and real pore framework. And the quantitative model on the crystallite size, specific surface area and pore volume was founded to interpret the change of specific surface area as well as make it possible to predict the data about the pore structure. Keywords titania, mesoporous, specific surface area, crystallite size 1 通讯联系人：Tel:(025 E-mail:xhlu@njut.edu.cn 基金项目：国家杰出青年科学基金）、国家自然科学重点基金）、国家自然科学基金 ） 引 言 近年来，纳米二氧化钛和具有纳米级孔道结构的二氧化钛由于其独特的量子效应、半导 体光催化性质及在诸多领域中的应用前景，已经引起了人们的广泛关注。与普通材料相比， 两者反应活性的增强主要来自于纳米晶导致的高比表面积的贡献[1]。纳米尺度二氧化钛的晶粒 大小直接决定其比表面积，晶粒尺寸越小，比表面积越大，表面活性中心及表面电荷传输速 率随之增加[2], 反应活性也随之提高。具有纳米孔道结构的氧化钛既可以作为纳米粒子的 “微 型反应器”，为纳米材料微观的研