纳米TiO2苎麻纤维复合功能材料的制备.pdfVIP

纳米TiO /苎麻纤维复合功能材料的制备 2 1,2 1,2 1,2? 刘 洋 ，刘忠文 ，刘昭铁 1 （陕西师范大学应用表面与胶体化学教育部重点实验室，西安710062 2 陕西师范大学化学与材料科学学院，西安710062 ） 摘要：以脱胶后的苎麻纤维为原料，钛酸丁酯为前驱体，无水乙醇为溶剂，通过表面胶凝过程，在苎麻纤维表 面形成了均匀的二氧化钛纳米级涂层。考察了反应时间，钛酸丁酯浓度对所得产品中二氧化钛含量的影响得出最 佳反应条件。通过红外光谱，x-射线衍射和扫描电子显微镜等方法对所得产物进行了表征。 关键词：复合材料；二氧化钛；苎麻 Preparation of Nano Titanium Dioxide/ Ramie Fiber Functional Composite Materials LIU Yang1,2 ，LIU Zhongwen1,2 ，LIU Zhaotie1,2 1 ( Key Laboratory of Applied Surface and Colloid Chemistry Shaanxi Normal University, Ministry of Education, 2 Xian 710062 ；School of Chemistry Materials Science, Shaanxi Normal University, Xian, 710062,) Abstract: A thin layer of titanium oxide has been produced on ramie fibres by the surface gelation process using ramie fibres as template, Ti(OnBu)4 as precursor and absolute ethanol as solvent. The influence of the reaction time and the Ti(OnBu) concentration on the TiO content of production had been investigated in detail, and the 4 2 optimum reaction conditions were obtained. The samples were characterized by FT-IR, XRD and SEM. Key words ： composite materials; titanium dioxide; ramie fibre 引 言 [1-3] 苎麻纤维是初生韧皮纤维，具有杨氏模量高、结晶度高、聚合度大和单纤维强度大等特点 。苎麻 纤维是优良的纺织原料之一，具有良好的穿着服用性能。苎麻纤维以单纤维形式进行纯纺或混纺，用作 服装类产品，具有凉爽、透气、易于吸湿散湿及抗菌防蛀的优点。但是，苎麻纤维对紫外光的吸收很弱。 众所周知，过量的紫外线照射会诱发皮肤病甚至皮肤癌，直接威胁人类的健康，因此，有关紫外线辐射 的防护成为当今的热点研究领域之一，其中，具有防紫外线功能的织物备受关注，已有利用二氧化钛包 覆棉纤维作为抗紫外纺织原料的研究报道[4,5] ，但是有关具有抗紫外功能的苎麻纤维复合材料的研究很少。 本研究通过苎麻纤维与二氧化钛的复合制备具有抗紫外线及抗菌功能的优良纺织原料。本研究以脱 胶后的苎麻纤维为原料，钛酸丁酯为前驱体，绝对乙醇为溶剂，通过表