ThermodynamicsAnalysisofMnO2toInfluenceEfficiencyof.pdfVIP

Thermodynamics Analysis of MnO2 to Influence Efficiency of Sulfur Fixing Agent CaO for Coal Powder Combustion Shengqin Zhang，Guangjun Zhu，Nengyun Deng，Zhongyu Liang School of Metallurgy and Materials Science and Engineering , Chongqing University of Science and Technology, Chongqing, China) E-mail address，shengqinzhang@163.com Abstract: For coal powder in southwest, sulfur fixing technology of coal powder combustion in this paper has been studied by thermodynamics calculation and experiment. Results show that, The efficiency of sulfur fixing of CaO in experiment is highest; when n(CaO)/n(S) ratio equal to 2.0, additive MnO2 enhances the efficiency of sulfur-fixing of fixing reagent CaO. MnO2 is easier to decompounds gradually to Mn2O3 and Mn3O4. one side the oxides of manganese can catalyze the reaction of sulfur-fixing , on the other hand Mn3O4 can absorbs SO2 to turn to MnSO4. Keywords: coal powder, sulfur fixing, CaO，MnO2，thermodynamics MnO2对煤粉中 CaO 固硫效率影响的热力学分析 张生芹 1，朱光俊 1，邓能运 1，梁中渝 1 重庆科技学院冶金与材料工程学院，重庆，中国，401331 Email address，shengqinzhang@163.com 摘 要: 本文针对西南地区使用的煤粉，通过热力学计算和实验研究发现：钙基固硫剂中以 CaO 的固 硫效率为最高；n(CaO)/n(S)=2.0 时，添加剂 MnO2的加入可以提高 CaO 的固硫效率。煤粉燃烧过程中 MnO2将逐级分解，分解产物为 Mn2O3、Mn3O4，锰的氧化物一方面可以催化 CaO 的固硫反应，另一 方面 Mn3O4本身也参与到固硫反应之中，生成 MnSO4。 关键词: 煤粉；固硫；CaO；MnO2；热力学 1 引言 煤粉燃烧是煤炭利用的主要方式，煤燃烧时会排 出大量 SOx、NOx、COx、重金属、可吸入粉尘等有 毒有害物质。我国煤燃烧所排放的硫化物(SOx)占到全 国燃料总排放硫化物(SOx)量的 85%，目前酸雨区域 已超过国土面积的 40%。因此，随着环境保护意识的 加强，煤的洁净燃烧技术已经成为我国解决环境问题 的主导技术之一，煤粉的燃烧问题也日益引起人们的 重视，控制煤粉燃烧过程中硫化物的排放，已成为煤 燃烧领域亟待解决的课题[1]。 本文通过热力学计算和 TG/DTA 实验，对钙剂固 硫剂 CaO 的固硫反应过程，以及添加剂 MnO2对某钢 铁厂用煤粉钙基固硫剂固硫效率的影响进行了分析。 2 CaO 的固硫机理概述 通过对 n(CaO)/n(S)=2.0 时 CaCO3 、CaO 和 Ca(OH)2 三种钙基固硫剂[2]的固硫率及钙利用率的对 比实验，得出了煤粉燃烧过程三种钙剂固硫剂的固硫 率和钙利用率，见表 1。 Table 1． efficiency of sulfur fixing of 3 different Ca-based sulfur fixing reagent and use ratio of calcium 表 1. 三种钙基固硫剂的固硫率及钙的利用率 CaCO3 CaO Ca(OH)2 固硫率(η) 58.56 62.62 62.30 钙利用率(λ) 29.33 31.58 34.36