金属间化合物Ti2AlNb的高温变形行为和变形机理.pdfVIP

Trans. Nonferrous Met. Soc. China 26(2016) 722−728 Thermal deformation behavior and mechanism of intermetallic alloy Ti2AlNb Qin-chai ZHANG1 1 1 1 2 3 , Ming-he CHEN , Hui WANG , Ning WANG , Jin-dong OUYANG , Xin-xiao LI 1. College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China; 2. Jiangxi Hongdu Aviation Industry Group Co., Ltd., Nanchang 330024, China; 3. Xi ’an Aero Engine (Group) Co., Ltd., Xi’an 710021, China Received 22 April 2015; accepted 26 October 2015 Abstract: The deformation behavior and mechanism of Ti2AlNb-based alloy were experimentally investigated at elevated temperatures. Firstly, the stress−strain relationships at different temperatures and strain rates were investigated via uniaxial tensile testing. Then, formability data, as determined by examining the deep drawing and bending abilities, were obtained through limiting draw ratio (LDR) and bending tests. Finally, metallographic experiments and fracture morphology investigations were conducted to examine the thermal deformation mechanism of the alloy. The results showed that as the temperature increased, the total elongation increased from 13.58% to 97.82% and the yield strength decreased from 788 to 80 MPa over the temperature range from 750 to 950 °C at a strain rate 0.001 s− 1. When the temperature reached 950 °C, the strain rate was found to have a great influence on the deformation properties. The plastic formability of the sheet metal was significantly improved and a microstructural transformation of O to B2 and α