非负载型NiMoW加氢催化剂的制备、表征和性能评价.pdfVIP

石油学报(石油加工) 2012年10月 ACTA PETROLEI SlNICA(PETROI。EUM PROCESSING SECTION) 第28卷第5期 文章编号：i001—8719(2012)05—0730—09 非负载型NiMoW加氢催化剂的制备 表征和性能评价 孔 妍，殷长龙，柳云骐，赵瑞玉，张孔远 (中国石油大学重质油国家重点实验室CNPC催化重点实验室， ，王嘉玮，刘 山东青岛266580) 、 晨光 摘要：以NiMoW复合氧化物为前躯体制备高活性非负载型NiMoW加氢催化剂，考察了制备过程中黏结剂、胶 溶剂、熟化处理等因素对催化剂性能的影响。采用BET、XRD、SEM、TEM、强度测定、堆密度测定等手段对 催化剂进行表征，采用模拟柴油体系和真实柴油为原料对催化剂进行活性评价。结果表明，选择合适的黏结剂、 胶溶剂以及适宜的熟化处理方法，不但可以保持催化剂原有活性相结构，而且能减小催化剂颗粒度，增大比表面 积及孔容、孔径，提高催化剂的机械强度。在345(2、7．0 MPa、空速2．0 h-1条件下，采用熟化处理制备的 NiMoW-H催化剂，可将柴油中的硫质量分数由3690 pg／g降低到9 pg／g，而NiMoP／AIz0。参比催化剂仅降低到 103#g／g。 关键词：非负载型催化剂；柴油；超深度加氢脱硫；NiMoW)熟化 中图分类号：TE624．93 文献标识码：A doi：10．3969／j．issn．1001-8719．2012．05．005 Preparation，Characterization and Catalytic Performance of Unsupported NiMoW Hydrotreating Catalyst KONG Yan，YIN Changlong，LIU Yunqi，ZHA0 Ruiyu，ZHANG Kongyuan， WANG J iawei。LIU Chenguang (State Key Laboratory of Heavy Oit Processing，Key Laboratory of Catalysis of CNPC， China University of Petroleum，Qingdao 266580，China) Abstract：Highly active unsupported NiMoW catalysts were prepared with NiMoW composite oxide as precursor．The effects of binders，peptizators and mature conditions on the performance of NiMoW catalysts were investigated．Nitrogen physisorption measurement(BET)。X—ray diffraction (XRD)，scanning electron microscopy(SEM)，transmission electron microscopy(TEM)，strength test and bulk density test were used to characterize the NiMoW catalyst，and its catalytic activity was evaluated with the simulated diesel system and diesel as the feed．The results showed that proper choice of binder，peptizator combined with proper way of maturation could reduce the particle size of the NiMoW catalysts without damaging the original structure of crystals，further improve the properties of catalyst，such as enlarging its specific surface area，pore volume，pore size distribution and enhancing its mechanical strength．Under the conditions of temperature 345℃。 hydrogen pressure 7．0 MPa and liquid hourly space velocity(I。HSV)2．0 h 1，with the NiMoW—H prepared