粘度对氧化铁纳米流体氨水降膜吸收的影响.docVIP

Sustainable Development 可持续发展, 2011, 1, 45-49 /10.12677/sd.2011.12008 Published Online July 2011 (/journal/sd/) The Effect of Viscosity on the NH /H O Falling Film 3 Absorption with Fe O Nanofluid 2 * 2 3 Liu Yang, Kai Du, Yanjun Li School of Energy and Environment, Southeast University, Nanjing Email: windy4ever@163.com Received: Apr. 17th, 2011; revised: Jul. 5th, 2011; accepted: Jul. 11th, 2011. Abstract: The effect of viscosity on the heat and mass transfer of NH /H O falling film absorption with 3 2 Fe O nanofluid is studied. The results show that, the viscosity, influenced by the ingredient of nanofluid, di- 2 3 rectly influence the performance of absorption. The heat and mass transfer of absorption, is weakened by high viscosity nanofluid of only adding sodium dodecyl benzene sulfonate (SDBS), while, enhanced by lower vis- cosity nanofluid with appropriate ingredients. The nanofluid with lowest viscosity, prepared by adding 0.2% Fe O and 1.5% SDBS, achieves the optimal performance in mass and heat transfer. 2 3 Keywords: Viscosity; Nanofluid; Falling Film Absorption; Fe O3 2 粘度对氧化铁纳米流体氨水降膜吸收的影响* 杨 柳，杜 垲，李彦军 东南大学能源与环境学院，南京 Email: windy4ever@163.com 收稿日期：2011年 4月 17日；修回日期：2011年 7月 5日；录用日期：2011年 7月 11日 摘 要：本文研究了粘度在氧化铁纳米流体管外降膜吸收氨气过程中对传热传质的影响。结果表明： 纳米流体的组分直接影响着纳米流体的粘度，而粘度又直接影响着氧化铁氨水纳米流体降膜吸收过程 中传热传质的性能。只添加表明活性剂十二烷基苯磺酸钠(SDBS)会使流体粘度增加，从而导致吸收过 程传热传质效率的降低；而添加适当的 SDBS和纳米氧化铁能获得较低粘度，从而强化传热传质效率。 实验表明氧化铁和 SDBS质量分数分别为 0.2%和 1.5%的时候，制得的纳米流体具有最低的粘度和最高 的传热传质性能。 关键词：粘度；纳米流体；降膜吸收；Fe O3 2 1.引言 铜氨络离子，很难在氨水中长期稳定存在。 2007 年 Yong Tae Kang [4] 等人进行了在氨水中添加碳纳米管 纳米流体既是指纳米颗粒悬浮液，是 Choi SUS[1] 在 1995年首先提出。随着纳米材料科学的迅速发展， 纳米流体在传热和传质两方面的强化作用也逐渐应用 到氨水吸收系统中。目前国内外已经有学者对一些纳 米材料应用于氨水中，对其进行了稳定性研究，或者 通过鼓泡吸收等方式进行研究，取得了较为理想的结 果。2006年 Jin-Kyeong Kim和 Jun Young Jung 进行 了在氨水溶液中添加 Cu和 CuO纳米颗粒和表面活性 剂的鼓泡吸收实验，结果表明单纯加入纳米颗粒吸收 率可提高到 3.21倍；同时加入纳米颗粒和表面活性剂 可提高到 5.32倍，但由于纳米颗粒都与氨水反应生成 的鼓泡吸收实验，结果显示在添加了 0.001 wt%的碳 纳米管后氨水的吸收过程的传热和传质效率分别提高 了 20%和 29.4%。苏风民、陈嘉宾 等人通过对碳纳 米管的