垃圾焚烧灰渣对电镀废水中重金属的吸附特性.doc

拟再审修改稿 稿件编号：200707043 垃圾焚烧炉渣对电镀废水中Cu的吸附特性 陈华林 周江敏 黄崇宝 潘传信 （温州大学生命与环境科学学院，温州 325027） 摘 要 以垃圾焚烧炉渣作吸附剂，对电镀废水中Cu的吸附特性进行了研究，包括吸附速率，解吸速率，吸附等温线，连续柱吸附实验等。结果表明，炉渣对电镀废水中Cu的吸附平衡时间和解吸平衡时间均为8h。炉渣对Cu的吸附等温线为直线型，可用Henry型方程进行拟合。连续柱吸附实验结果表明，炉渣对电镀废水在连续吸附55h后吸附能力逐渐丧失，累计最大吸附量为921/g，而炉渣对人工配水在连续吸附80h后吸附能力完全丧失，累计最大吸附量为2687/g。 关键词 炉渣 电镀废水 吸附 Cu 中图分类号：X703 文献标识码：A 文章编号： The Sorption Properties of Cu in Electroplating Wastewater on Municipal Solid Waste Incinerator Bottom ash Chen Hualin Zhou Jiangmin Huang Chongbao Pan Chuanxin (School of Life and Environmental Sciences, Wenzhou University, Wenzhou, 325027) Abstract: The sorption properties of Cu in electroplating wastewater on municipal solid waste incinerator bottom ash were studied using the experiments of sorption rate, desorption rate, equilibrium sorption and continuous column sorption. The results showed that the equilibrium time of sorption and desorption experiment were 8h. The equilibrium sorption curve was linear, which could be modeled with Henry equation. The result of continuous column sorption showed that for the electroplating wastewater, after 55h, the sorption capacity of bottom ash declined gradually, and the total adsorbed Cu in bottom ash reached 921/g; while for the model wastewater, after 80h, the sorption capacity declined gradually and the total adsorbed Cu reached 2687/g. Keywords: bottom ash; electroplating wastewater; sorption; Cu 垃圾焚烧炉渣是城市垃圾焚烧后产生的固体废弃物，其物理化学性质取决于燃烧物体的性质、燃烧方式以及燃烧温度等，主要化学成分为SiO2和Al2O3，此外还有少量CaO、Fe2O3、MgO等，呈碱性[1]。目前对炉渣的利用主要是用作建筑材料，如用作石油沥青路面的替代骨料、水泥/混凝土的替代骨料等[2,3]。 炉渣呈多孔蜂窝状，有较大的表面积，有一定的吸附能力，是一种廉价的吸附剂，有时可以代替活性碳、硅胶、活性Al2O3等作专用吸附剂，对许多有机污染物及废水中的重金属离子均有良好的吸附能力[4,5]。 用炉渣做吸附剂处理废水是一种“以废治废”的思路，可大大降低废水的处理费用，实现环境效益与经济效益的统一。本研究以垃圾焚烧炉渣作吸附剂，用来处理电镀废水中的重金属离子，探讨其对电镀废水中重金属的吸附特性，为开发垃圾焚烧炉渣作废水处理吸附剂提供理论依据。 1 材料与方法 1.1 炉渣和电镀废水 实验用的炉渣样品取自温州临江垃圾发电厂，该厂使用的是自己开发的HWM二段往复式炉排垃圾焚烧炉过目筛1 柱实验装置图 Fig.1 The equipment of column experiment 2 结果与讨论 2.1 炉渣的基本理化性质和重金属的浸出特性 炉渣的基本理化性质测试结果见表1。从表中可以看出，该