单辊破碎机星轮铸造工艺设计及模拟优化.pdfVIP

学兔兔 铸造工艺 单辊破碎机星轮铸造工艺设计及模拟优化 米国发，王锦永 (河南理工大学 材料科学与工程学院，河南 焦作 454000) 摘要：运用传统的铸造工艺设计方法对星轮铸钢件铸造工艺进行了初步设计，利用Z-Ca St模 拟软件，对星轮初始_T-艺的凝固过程进行了模拟，分析了初始工艺产生缺陷的部位和原因。在 此基础上通过调整冒口尺寸和分布，进行工艺优化，最终获得了合适的工艺方案。模拟结果显 示，优4~_T-艺实现了星轮的顺序凝固，消除了缩孔、缩松缺陷。 关键词：星轮；铸造工艺；数值模拟；z—Ca St软件 中图分类号：TG24 文献标识码：A 文章编号：1 673—3320(2009)05—0015-04 Numerical Simulation and Optimization of Technological Design for Single Roll Crusher Star Wheel Mi Guofa，Wang Jinyong (College of Material Science and Engineering，Henan Polytechnic University, Jiaozuo 454000，Henan，China) Abstract：The original foundry technique of the star wheel was designed by conventional design method． The progress of solidification of original foundry technique of star wheel was simulated by the Z—Cast SOftware．The location and the cause of the shrinkage defects of original technology were analyzed． Based on this，the size and position of risers were changed for process optimization and the reasonable foundry technique was designed finally．The result shows that the optimized technology can ensure castings progressive solidification and eliminate the shrinkage and the porosity． Key words：star wheel；casting process；numerical simulation；Z—Cast software 单辊破碎机主要用于烧结厂对烧结矿进行破 环境非常恶劣，破碎的烧结矿温度高达600℃以 碎处理，以满足高炉生产的需要。其星轮的工作 上，并且承受着很大的摩擦力和冲击力。尽管星 基金项目：河南省杰出人才创新基金 (项目编号：0621000700) 摩擦系数降低，从而降低了百公里油耗，延长了 使用寿命。生产企业正在努力攻关，使缸套的使 用寿命超过50万km，达到欧洲汽车制造的水平。