新型铸造用α淀粉／月彭润土复合粘结剂制备及应用.pdfVIP

学兔兔 OCt．2008 VO1．57 NO．10 新型铸造用Oc一淀粉／月彭润土复合粘结剂制备及应用 郑玉婴，程 雷，吴章宏，陈玉琳 (福州大学化学化工学院，福建福州350002) 摘要：以木薯淀粉为主要原料，自行研制的有机膨润土为改性剂，经过熔融和溶液插层等工艺制备木薯淀粉／膨润土 复合粘结剂。采用FTIR、XRD手段表征及力学性能测试，结果表明，该复合粘结剂具有粘结强度高、抗吸潮性好等性 能，且成本低、工艺简单和环境友好。 关键词：木薯淀粉；膨润土；铸造用粘结剂 中图分类号：TG221 文献标识码：A 文章编号：1001—4977(2008)10—1017—04 Preparation and Application Of New Kind of Tapioca Starch／Bentonite Composite Casting Binder ZHENG YU—ying，CHENG Lei，WU Zhang—hong，CHEN Yu—lin ． (College of Chemistry and Chemical Engineering，Fuzhou University，Fuzhou 350002，Fujian，China) Abstract： Using tapioca starch as main material and the seIf—deveIOped organic—bentonite as modifier，tapioca starch／bentonite composite binder was made by melting and solution intercalation technologies．The binder was characterized by means of FTIR．XRD and mechanicaI performance test．The results show that this nanometer composite binder has not only high bond strength，good humidity resistance，and excellent collapsibility，but also IOW costs，simple process and environment friendly characteristic． Key words：tapioca starch；bentonite；casting binder 铸造工业是我国国民经济中的一个重要产业，粘 量取蒸馏水快速搅拌，直至将其充分溶解。将烧杯中 结剂及其使用技术则是影响砂型铸造生产环境和铸型 的溶液倒人烧瓶中对应的温度下反应一段时间后，将 性能的主要因素，所以研制新型无毒无污染，综合性 反应后的土浆从烧瓶中倒出，减压抽滤，用蒸馏水洗 能优良的铸造粘结剂及其造型、制芯工艺势在必行[1_2】。 涤，所得滤饼在80～105℃下烘干、粉碎、过筛，得到 淀粉是一种天然多糖高聚物，是由葡萄糖失水缩合而 白色有机膨润土粉末。 成的高分子化合物，是重要的绿色化学品而且资源丰 1．3 PVA改性有机膨润土 富，成本低，使用方便，以淀粉为主的粘结剂研究具 将上述有机膨润土粉末加计量水，在边搅拌边逐 有非常重要的意义。已经有不少学者在这方面做了研 步加入已预先加温熔解 (浓度为10％的PVA溶液)的 究M，但是采用有机膨润土改性淀粉制备淀粉／膨润土 助插层剂，继续不断搅拌，搅拌反应时问为1～3 h，将 复合粘结剂并应用于型芯砂的粘结尚未见报道。