消失模铸造涂料性能影响因素的研究.pdfVIP

学兔兔 2013年第6期 铸 造 设 备 与 工 艺 2013年 12月 FOUNDRY EQUIPMENT AND TECHNOLOGY · 消失模与V法铸造· 消失模铸造涂料性能影响因素的研究 陈学更，韩 文，朱劲松 (宁夏共享化工有限公司，宁夏银川 750021) 摘 要：对影响消失模铸造涂料性能的耐火材料目数、黏结剂、表面活性剂及其加入量等因素进行了实验， 并利用硅藻土作为吸附剂，考察硅藻土的加入量对消失模铸件表面碳缺陷的影响。通过实验，获得较佳的消失 模铸造涂料的制备条件，并加入能够吸附聚苯乙烯裂解产物的吸附剂，从而减少了消失模铸造的碳缺陷。 关键词：消失模铸造；消失模涂料；透气性；吸附剂；碳缺陷 中图分类号：TG249 文献标识码：A 文章编号：1674—6694(2013)06—0022—03 Study on the Factors Affecting the Performance of the EPC Coating CHENXue-geng，HAN Wen，ZHUJin-song (NingxiaKocel Chemicals CO．，LTD，YinchuanNingxia 750021，China) Abstract：The factors of mesh size of refractory material，binder，surface active agent and their content affecting the property of EPC coating were tested．The diatomite was added as adsorbent，the influence of its content on carbon defect on the casting surface was investigated．Through experiments，the better coating production process was obtained and the adsorbent to adsorb the pyrolysis products of polystyrene was added to reduce the carbon defects of EPC． Key words：EPC，EPC coating，gas permeability，adsorbent，carbon defect 消失模铸造(简称为EPC)，又称为实型铸造， 实验原料：酸洗铝矾土(w(A1 0，)≥88％))、白 是将涂有涂料的泡沫塑料(EPS)模样埋入无黏结剂 云母(白度≥85％，oJ(A1 0 )≥60％)、硅藻土、凹凸棒 的干砂中造型，采用微震加负压紧实，在基本没有 土、水性氨基树脂、白乳胶(聚醋酸乙烯乳液)、木质 型芯的情况下浇入液态金属，并在浇注和凝固过程 素磺酸钠、聚丙烯酰胺、磷酸三丁酯、五氯酚钠、氧 中继续维持一定的负压值，泡沫气化，继而被金属 化铁、平平加(脂肪醇聚氧乙烯醚)、Triton x一102、软 液取代形成铸件的一种新的铸造成型方法lll。涂料 水。所用原料均为工业级。 在消失模铸造中起着非常重要的作用，直接影响着 分析仪器：NDJ一5s旋转黏度计、型砂透气性测 铸件的质量。 定仪、发气量测定仪、涂料耐磨性测定仪等。