铜合金真空差压铸造设备的研制.pdfVIP

学兔兔 Feb．2011 铸 造 VOI．6O NO．2 FO RY ● -· ^ ● ^ ^ - ‘ ^ I{铸造设备 } ． ． ，． ．， ，， ～ j 铜合金真空差压铸造设备的研制 游 龙，王自东，冯 建，王 超，林国标 (北京科技大学材料科学与工程学院，北京100083) 摘要：自主开发了铜合金真空差压铸造设备，对设备主体、升液管结构、中隔板与升液管之间的密封等进行了优化设 计，使其满足真空差压铸造铜合金的工况条件，并通过此设备成功制备出合格的金属型端盖铸件以及熔模叶轮铸件。 关键词：真空差压；铸造设备；铜合金 中图分类号：TG233．1+3 文献标识码：A 文章编号：1001—4977(2011)02—0167—04 Development of Vacuum Counter-Pressure Casting Equipment for Copper Al loys YOU Long，WANG Zi—dong，FENG Jian，WANG Chao，LIN Guo-biao (School of Materials Science and Engineering，University of Science and Technology Beijing， Beijing 1 00083，China) Abstract：The seIf．deveIOped vacuum cOunte卜pressure casting equipment for copper alloys was presented to satisfy the working condition of casting copper alloys，the main body of the equipment， structure of riser tube。sealing between riser tube and center suppo~panel were optimized．Finally， castings of cover and jmpeller were successfully produced by using permanent mold and investment mold，respectively with this equipment． Key WOrds：vacuum counter—pressure；casting equipment；copper alloy 现阶段对真空差压铸造设备主要用于铝合金、镁 能指标如下： 合金等轻金属的研究上，基于铜合金真空差压铸造设 (1)真空差压铸造设备的主体部分包括：上下罐、 备的研制较少，主要由于铜合金与铝合金相比，在物 卡环锁紧环节、中隔板、反射屏、电极系统、升液管、 理性质及熔炼技术上有较大的困难，主要包括：①铜 各个密封环节、加料机构、保温炉升降机构； 的熔点高 (1 083℃)、铝合金的熔点低 (660℃)； (2)设备的附属部分包括：吊车、工作台、上下 ②铜合金的密度比铝合金的密度大3倍多；③二者的熔 罐保温炉、感应炉、坩埚、安全阀、压力表、压力传 炼技术存在很大差异：铝合金需精炼处理、变质处理 感器、热电偶、液压系统、气泵、真空泵、储气罐和 和孕育处理，而铜合金需去气处理和脱氧，而且铜合