论粉末冶金材料的密度测定.pdfVIP

学兔兔 第 2O卷第6期 粉 末 冶 金 工 业 VoI_20 NO．6 2010年 12月 POWDER M ETALLURGY lNDUSTRY Dec．2O1O 论粉末冶金材料的密度测定 王崇琳 (中国科学院金属研究所，沈阳 110016) 摘 要：密度是粉末冶金材料的最重要基础数据，它对其物理和机械性能影响极大。在用排水 法测定密度时，要注意排除系统和偶然误差，特别应注意考虑开通孔洞的影响，否则计算出的 密度值将会偏高，结果是不真实的，开孔愈多，浸入水愈多，则其偏差愈大。 关键词：密度测定；排水法；开孔孔隙度 中图分类号：TF12 文献标识码：A 文章编号：1006—6543(2010)06—0001一O4 oN THE MEASUREMENT oF DENSITY FoR P／M MATERIALS W ang Chong-lin (Institute of Metal Research，Chinese Academy of Sciences，Shenyang 1 1 00 1 6，China) Abstract：The density is one of the most important properties for P／M materials as it has de— cisive effects on its physical and mechanical properties．In order to measure the real value，we should avoid any systematic and accidental errors in the procedure of density determination if using immersed method in water．Especial notice should be paid to the effect of open porosi— ty，as it would bring higher calculating results of density．More open porosity would result in more impregnated water，and more false result of the density． Key words：Measurement of density；Immersed method in water；Open porosity 密度是粉末冶金材料的最普通却是最重要基础 一 个相对密度约90 的粉末冶金材料，准确测定密 数据，它对其物理和机械性能，特别是韧性和疲劳影 度是非常重要的。 响极大。例如，Distaloy AB+0．5 C烧结材料在 密度为7．0 g／cm。时，抗拉强度为600 MPa，冲击韧 1 排水法测定密度时的主要方法 性为3O J，密度提高到 7．2 g／cm。时，其值分别为 660 MPa和 50 Jl】j，由此可见，在材料相对密度 排水法是测定密度的主要方法，阿基米德原理 89 时，密度提高 2．9 ，抗拉强度提高 10 ，冲击 是很简单的，物体在空气和水中的质量差表现为浮 韧性提高 1．7倍。又如，有人研究了 0．5C一1．5Cu一 力，它相应于排开同体积水的质量。硬质合金材料 0．55Mo一2．ONi材料的疲劳性能_2 j，当密度为 6．9