学兔兔 2014年第3期 混凝 土 与 水 泥 制 品 2014 No．3 3月 CHINA C0NCRETE AND CEMENT PRODUCTS March 废旧聚苯颗粒改性水泥砂浆力学性能研究 李启强，张海波，李明远，芦 昊 (河南理工大学材料科学与工程学院，焦作454000) 摘 要：以废旧聚苯颗粒等体积取代水泥砂浆中的砂子，研究了废旧聚苯颗粒掺量对水泥砂浆静力学性能的影 响。结果表明，随聚苯颗粒掺量增加，砂浆流动度先增加后下降，砂浆试样7d、28d抗折抗压强度均呈下降趋势，3d抗 折强度先增加后下降，抗压强度下降缓慢：砂浆试样3d、7d、28d抗压强度与密度存在线性关系，且线性关系都比较 显著。 关键词：废旧聚苯颗粒：砂浆；力学性能；线性关系 Abstract：The influence of the content of waste polystyrene granule which substitutes the equivalent content for sand in mortar on physical properties of cement mortar is studied．It shows that with the increasing of polystyrene granule ag— gregate content，the fluidity of cement mortar firstly increases and then decreases；The 7d，28d of flexural and compressive strength of samples are on the decline，but its 3d flexural strength first increases and then decrease，meanwhile，the 3d compressive strength of cement mortar show a slow downward trend；it has a very significant linear relationship between the 3d，7d，28d of the compressive strength and density of samples． Key words：Waste polystyrene granule；Mortar；Physical properties；Linear relationship 中图分类号：TU528．2 文献标识码：A 文章编号：1000—4637(2014)03—76—03 0 前言 粒粒径在1~5mm之间，如图1。 聚苯颗粒(简称EPS颗粒)是由废弃的聚苯乙 水：自来水。 烯塑料经加工制成，具有耐老化、抗腐蚀、无法自然 降解的特点[ ，且使用多为一次性，许多废弃EPS 由于处理与降解困难成为城市固体垃圾．对环境造 成严重的污染。同时，EPS具有颗粒密度低、热工性 能好等特点I3J，通常利用EPS颗粒取代传统骨料配 制轻骨料砂浆。近年来的研究l4_5l表明，以EPS颗粒 作为主要原料制备的保温砂浆是一种性能良好的 保温材料，但大部分学者集中研究EPS颗粒对砂浆 的保温性能影响．对砂浆力学性能以及应用研究较 少。为此，本文研究了废I13的EPS颗粒掺量对水泥 砂浆力学性能的影响，以期为废旧聚苯颗粒在水泥