研究与技术 磁控静电纺聚丙烯腈纤维及其微观结构 吴 玥 （上海政法学院 经济管理系，上海 201701） 摘要：利用新型磁控静电纺丝方法对聚丙烯腈进行纺丝试验研究，分别在不同的电压条件下引入磁场，通过比较引入磁场前后的纤维 形貌、纤维结晶度及纤维力学性能，来研究磁场对纤维微观结构及性能的影响。结果表明：磁场对纺丝结果有一定的影响，随着磁场 的引入，纤维平均直径减小、结晶度增大、断裂强度增大。 关键词：静电纺丝；磁场；直径分布；结晶度 中图分类号：TB383；TQ340.64 文献标识码：A 文章编号：1001-7003（2009）10-0038-03 Study on Magnetic Control Electrostatic Spinning Polyacrylonitrile Fibers and its Microstructure WU Yue （Department of Economic and Management, Shanghai University of Political Science and Law, Shanghai 201701, China） Abstract: Polyacrylonitrile was researched with new magnetic control electrostatic spinning. Under different voltage conditions, the experiment introduced magnetic field and compared the fiber’s shape, crystallinity and mechanical property before and after introduce magnetic field, to research the effect of magnetic field to fiber microstructure on the aspect of structure and property. The results showed: magnetic field had some effect to the result of spinning, with the introducing of magnetic field, average diameter of fiber decrease, crystallinity raised and breaking strength raised as well. Keywords: Electrostatic spinning; Magnetic field; Diameter arrange; Crystallinity 静电纺丝是聚合物溶液或熔体在静电场作用下进行 置好的PAN纺丝溶液进行静电纺丝，调节纺丝工艺条件 喷射、拉伸而获得纳米级纤维的纺丝方法。这种纺丝技 参数，根据试验方案设定纺丝电压、接收距离、励磁电 术有着许多独有的特性，目前已成为开发超细纳米纤维 流的大小，得到不同条件下的静电纺纳米纤维样品。 及其复合材料的应用热点[1-3]。磁控技术是一种应用领 域比较广泛的技术，磁场是一种具有特殊能量的场，与 受控对象作用产生力，在宏观上改变其运动状态，在微 观上改变其结构[4-6]。 本研究将两种技术结合，在传统静电纺丝装置的 基础上，引入了磁场发生控制器件[7-8]，以聚丙烯腈 （PAN）为原料进行试验，主要考察磁场对静电纺纤维 的外观形态以及微观结构的影响。 1 试 验