怎样改善尼龙注塑件的变形问题(国外英文资料).docVIP

怎样改善尼龙注塑件的变形问题(国外英文资料) How to improve the deformation of nylon injection molding (1) jig with cooling water; Die design problem Review the design of parting and gate 1. The crack Crack is a common defect of plastic products, and the main reason is due to stress deformation. It mainly has the stress distortion of residual stress, external stress and external environment. (-) the cracking of the residual stress Residual stress is caused mainly by the following three conditions: overfilling, ejection and metal inserts. As a result of the cracks in the pack, the solution is mainly in the following areas: (1) due to the pressure loss minimum sprue, so, if the occurrence the main cracks near the sprue, can consider to switch to a multipoint distribution points gate, side gate and handle gate way. (2) in guarantee under the premise of resin decomposition, degradation, can raise the temperature of the resin melt viscosity reduction, improve liquidity and, at the same time also can reduce the injection pressure, to reduce stress. (3) in general, the temperature of the die is easy to produce when the temperature is low, and the temperature should be raised properly. But when the rate of injection is high, even if the temperature is low, the stress can be reduced. (4) the duration of injection and overpressure can also result in stress, which is better for shortening or carrying out the THR. (5) the non-crystalline resin, AS resin, ABS resin, PMMA resin such AS a crystalline resin such AS polyethylene, polyformaldehyde is easy to produce residual stress should be attention. Stripping out, because the draft small punch, plastic moulding and rough, make out force is too large, produce stress, even sometimes around the puller bleaching or fracture phenomenon. If you look closely at the location of the crack, you can determine the cause. It is most likely to be stressed when the injection molding is embedded in the metal, and it is easy to be cracked after a period of time. This i