以镍代银的空气烧结镍导体浆料.doc

2000 年 3 月 第 21 卷第 1 期 贵 金 属 　　　　　　　　　　　　　　　 Precious Metals Mar. 2000 　　　　　　　　　　　　　　　 Vol. 21 , No. 1 Ξ 以镍代银的空气烧结镍导体浆料 谭富彬 　赵 　玲 　王昆福 　张振中 　黄富春 　李 　茜 (昆明贵金属研究所 , 中国昆明 　650221) New Nickel Conductor Pastes Sintered in Air Tan Fubin , Zhao Ling , Wang Kunfu , Zhang Zhenzhong , Huang Fuchun , Li Qian ( Kunming Institute of Precious Metals , Kunming 650221 , China) Abstract 　The new nickel conductor pastes were prepared through sinter in air. The properties and the successive operation life of two kinds of nickel pastes produced by different methods were studied parallelly. The comparison testes show that the nickel paste prepared by chemical method is suitable to use for DC plasma displays , the nickel pastes can be used as a substitute for silver paste. Keywords 　Nickel paste , Silver paste , Nickel conductor , Sinter 摘 　要 　介绍了空气烧结镍浆的制备 , 比较两种不同制备方法获得的镍浆性能及连续工作 寿命。在直流等离子显示板中宜使用化学法制备的镍浆 , 而且可代银电极。 关键词 　镍浆 , 银浆 , 镍导体 , 烧结 分类号 　TG146. 36 　文章编号 　1006 - 0676(2000) 01 - 0022 - 04 1 　前 　言 直流等离子平板显示器反映了当代仪器仪表的进步。原先是用指针指示测量物理参数(如温度、 压力等) 。发光二极管的问世 , 用发光二极管取代指针式指示。随着厚膜技术的发展及应用 , 人们 根据惰性气体在直流电场中放电发光原理 , 制成了直流等离子平板显示器 , 比前面两种显示方法又 进了一步。即清晰度、体积及重量有了明显改进。原先显示板阴极用银浆印刷、烧结后获得 , 阳极 是蒸镀二氧化锡薄膜。印刷银浆线分辨率为 0125～0130mm。仪表工作时 , 显示板被施加 200～350V 的直流电压 , 此时银电极间会发生溅射导致短路 , 显示板寿命终止。因而银电极被陶汰。镍是耐电 流电压轰击不可多得的阴极材料。人们最初用保护气氛烧结制成了显示板镍电极。笔者用添加硼等 元素的方法制成了空气烧结镍导体 , 其中有粉末冶金法及液相化学制备法[1] 。本文着重讨论 2 种方 法制备镍导体性能比较。 2 　实 　验 211 　镍粉制备 : 粉末冶金法按作者发明专利的方法制备。液相化学反应法 , 是用含硼的 化合物与镍盐反应制成 Ni2B 粉末。 Ξ 1999 —02 —23 收稿  贵 　金 　属 23 212 　镍导体的制备 : 在镍粉中添加低熔点玻璃按重量比 2 %～8 % , 余为镍粉。用乙基纤维素松油 醇作有机粘合剂 , 约占总重量 14 %～16 % , 混合轧制成浆料 , 然后丝网印刷、烘干 , 在 570～ 600 ℃空气烧结得导电图案(显示板基片是窗玻璃板) 。 213 　两种镍浆的烧结 : 将粉末冶金法(样品 1 # ) 及化学法(样品 2 # ) 印制图案分别在 550、570、600、 640 ℃的温度进行烧结 , 冷却后测定电性能。 214 　粉末的物相 : 用日本理学 D/ max - RC 型 X - 射线衍射仪 , 工作条件 : Cu 靶 , 管压 40kV , 管 流 80mA , 石墨单色器 , DS 为 1 度 , RS 为 013mm , ss 为 1 度 , 对样品进行 X - 射线衍射分析。 3 　结果与讨论 311 　两种粉末的相结构 : 用作者专利制备的粉末 , 通过 X - 射线衍射分析 , 粉末中主体 是纯镍 , 同时有 Ni3B、NiB 玻璃体存在 , 也有少量 AlNi 及 AlB2