多孔材料不同孔隙百分比对压制变形规律的研究.pdfVIP

材料热处理技术IMaterial Heat Treatrnent 2012 年 10 月 多孔材料不同孔隙百分比对压制变形规律的研究 梅升，李勇 (华北水利水电学院机械学院，河南郑州 450045) 摘 要:针对多孔疏松材料在 SHS 烧结后致密化成型过程中工艺参数难以控制这一特性，采用 ANSYS 模拟了孔 隙体积百分比不同、压坯压下量为 30%时疏松孔的变形情况。通过分析变形区应力应变分布、孔形状、尺寸变化以及材 料变形力的变化，得出了不同孔隙百分比对加压变形情况的影响规律。 关键词:多孔压坯;压制变形;孔隙度;有限元模拟 申图分类号:TG301 文献标识码:A 文章编号: 1001-3814(2012)20-0026-04 Research on Densifica咀on of Porous Compacts with DitTerent Reduction Rate MEI Sheng, LI Yong (School of Mechanical Engineeri吨， Nor也 China University of Water Conservancy and Elec位ic Power, Zheng油ou 450045 , China) Abs仕act:A回归19 at the densification process of porous unconsolidated materials sintered by SHS，吐le compacts were simulated by 缸ite element analysis. The ANSYS was applied to simulate the deformation situation of the compacts under the press amount of 30% , and the 0也er conditions were constant. From the deformation and the dirnensional change, the equivalent strain and strain distrlbution in the deformation zone were analyzed and the variation law ofhole-existing materials deformation was summarized. Key words :porous compacts; forging deformation; porosity; finite element simulation φ80mm，在真空烧结炉中，采用铁合金 Ti-6Al-4V 母 自蔓延高温合成技术(SHS)是 21 世纪材料制备 含金粉，通过在真空炉内发生自蔓延高温合成反应， 领域的前沿方法，近年来利用 SHS 技术先烧结后压 可得到非致密化烧结多孔坯料，多孔坯料的孔径一 制来制备硬质合金越来越广泛，其具有很大应用前 景[1-2J 。通过自蔓延高温合成反应后生成多孔压坯为 般都小于 0.3mm，本次实验孔径采用 0.3mm。 对于烧结多孔金属材料，当孔隙度降低到 8% 非致密化材料，为了提高粉末冶金材料的性能，须对 时，孔隙基本上都是封闭的闭孔[司，同时为简化模 其进行致密化和进一步成型加工。而压坯材料在塑