采气井口装置主要零部件的失效分析.pdfVIP

采气井口装置主要零部件的失效分析 陈 浩 （西南石油学院机械工程系，四川南充 637001） 摘要 对采气井口装置主要零部件的失效形式及失效模式进行了深入的分析，发 现失效形式有：电化学腐蚀分布面积较大；冲蚀产生蚀槽；分布不均匀的坑蚀； 腐蚀产物使闸板卡死；阀杆与闸板或阀针联接处硫化物应力腐蚀，使阀杆断裂； 磨损或腐蚀造成表面损伤，材料流失，影响密封性；密封盘根老化、鼓泡，永久 变形；失效模式为：腐蚀、磨损及密封件老化；易损件有：针阀的阀针与阀座； 闸阀的阀板与阀座；针阀、闸阀的阀杆、密封盘根及轴承，并提出了改善采气井 口装置系统可靠性的措施。 主题词 采气井口装置；零部件；损坏；分析；可靠性 中图分类号 TE831.1 Failure Analysis for the Main Component Parts of Wellhead Equipment, JSWPI, 1998, 20(1):64～67 Chen Hao (Dept. of Mechanical Engineering, SWPI, Sichuan, 637001) This paper has made a thorough analysis for failure modes and failure causes of the main component parts of wellhead, and has found out the main failure modes (larger distribution area caused by corrosion of electrochemistry, corrosion groove produced by erosion; uneven distribution corrosion pit; gate segments jammed by corrosion product; valve rod crack caused by sulphide stress attack between valve rod and gate segment or valve needle; sealing property affected by surface damage or loss of material caused by wear orcorrosion; ageing or bubbling of permanently deforming of seal elements ) and failure causes (corrosion and wear and ageing of seal elements) and the damageable units (valve needle and valve seat of needle valve; gate segment and valve seat of gate valve; valve rod and seal elements and bearing of needle valve and gate valve) A measure of improving the wellhead reliability was achieved. Key words: Gas producing wellhead; Component parts; Failure; Analysis; Reliability 前 言 失效分析是提高产品质量的重要手段，是质量管理的重要环节。对采气井口 装置的失效形式和模式进行分析研究，系统地研究机件的失效类型、鉴别失效类 型的技术，预测及监控失效的方法，改进与预防失效的措施等；对产品一切可能 的失效形式，其发生的条件、控制与预防等有深刻的理解，将为开发和改进设备 设计，制造工艺，管理规范制定，技术推广等提供数据资料；为充分发挥现有设 备服役能力，故障诊断的分析、维修、更换等提供理论依据，为开展高压采气井 口装置的可靠性水平预测研究奠定了分析基础。 根据国内外资料及现场调研，采气井口装置的易损件有：针阀的阀针与阀座； 闸阀的阀板与阀座；针阀、闸阀的阀杆、密封盘根及轴承。 常见的失效模式为腐蚀、磨损及密封件老化。腐蚀包括：电化学腐蚀和硫化 物应力腐蚀。磨损包括：磨粒磨损、冲蚀磨损、粘着磨损、腐蚀磨损。 主要失效形式：(1) 电化学腐蚀分布面积较大，冲