Nb元素对β型Ti-Mo基合金显微组织、力学性能和铸造性能的影响.pdfVIP

Available online at www .sciencedirect. com _- 由 .~;.， ScienceDirect Scienc e E L SEVIER Press Trans. NonferrOllS Met. Soc. China 25(2015) 2214- 2220 Effect of Nb addition on micros甘ucture， mechanical properties and castability ofß-type Ti-Mo alloys 1 2 3 3 Ling-bo ZHANG , Ke-zheng WANG , Li-juan XU飞 Shu-long XIA0 , Yu-yong CHEN 1. Stomatology Department, 2nd Affiliated Hospital, Harbin Medical University, Harbin 150086, China; 2. Department ofRadiology, 4th Affiliated Hospital, Harbin Medical University, Harbin 150001 , China; 3. School ofMaterials Science and Engineering, Harbin Institute ofTechnology, Harbin 150001 , China Received 10 June 2014; accep时10 Apri12015 Abstract: To develop novel ß句pe biomedical titanium alloys, a series ofTi-15Mo-xNb alloys(x=O, 5, 10 and 15, mass 台action in %) were designed and prepared by using vacuum arc melting method. The present study focused on the effect of Nb addition on the microstructure , mechanical properties and castability of Ti- 15Mo alloy. Phase analysis and microstructure observation show that a11 the alloys consist of single ß phase and the equiaxed ß grain is refined with increasing Nb content. These ß-type Ti-) 5Mo-xNb alloys exhibit good plasticity and rather low compression elastic modulus (in the range of 18.388-19.365 GPa). After Nb addition, the compression yield strength of the a110ys increases. With increasing Nb content, the micro-hardness of the alloys decreases. The alloys exhibit obvious fibrous strip microstructure after cold compression deformation. The castabi1ity test shows