Mo含量对激光立体成形Ti-6Al-Mo系合金组织及硬度的影响.pdfVIP

Rare Metal Materials and Engineering Available online at www.sciencedirect. com Volume 42 , Issue 7 , July 2013 Online English edition of the Chinese language journal ScienceDirect Cite this article as: Rare Metal Materials and Engineering , 2013 , 42(7): 1332-1336 Influence of Mo Content on Microstructure and Microhardness of Laser Solid Formed Ti-6AI-Mo System Alloys Zhang Fengying , Chen Hong , Xu Yiku , Zhang Xuemin Changan Univeristiy, Xian 710064, Ch的a Abstract: The novel Ti-6Al-yMo (3三烂11) titanium alloys were deposited from blended Ti , Al and Mo powders using the laser solid forming (LSF) process and the microstructure and hardness of as-deposited layers were investigated. Results show that the volume fraction of the priorαcolony decreases and the microstructure changes from widmanstätten structure to basketweave structure with the increase of Mo content. Meanwhile , the average size and aspect ratio of the prior αlath decrease and the volume fraction of the secondary αlaths increases with the increase of Mo content. The microhardness of as-deposite layers was also measured , and it is found that the hardness of as-deposited Ti-6Al-yMo alloys increases predominantly linearly with the increase ofthe Mo content untill1 wt% Mo Key words: laser solid forming; blended elemental powder; Ti-AI-Mo alloys; microstructure Laser solid forming (LSF) is a promising technique blend of elemental powders and to create an alloy in suit which is developed