Nd对AZ31镁合金微观组织与力学性能的影响.pdfVIP

Rare Metal Materials and Engineering Available online at Volume 38 , Issue 1, January 2009 .· Online English edition of the Chinese language joumal 心， ScienceDirect Cite this a民ic(e as: Rare Metal Materials and Engineering , 2009. 38(1): 0007-0010. Effect of Nd on Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Li Mingzhao, Li Cong, Liu Xuguang , Xu Bingshe KeyLab伺tory of Interfa饵Scien臼and Engineering 的Advan佣d Materials of Taiyuan University of Technol句y， Ministry of Education, Tai- yuan University of Techno/啤弘， Ta伊uan 03∞124， China Abstraet: Effect of Nd on as-cωt microstructure and mechanical prop创es of AZ31 magnesium a1loy were inv甜igated by ICP, metallographic microscopy , SEM, EDS , XRD and mechanical measurement. The results show 也at the microcon旬nt of Nd added in AZ31 alloy could result in the formation of intermetallic ∞mpounds of AhNd and Mgl2Nd at 伊ain boundary and in a-Mg m由民， and the absorption rate of Nd reached 95%, which obviously refmed AZ31 a1 10y microstructure and 加由er improved mechanical pro阳ties. The AZ31 all町containing Nd showed a tensile s町ngth of245 MPa, a yield strength of 171 MPa and a elongation of 也. Key words: magnesium alloy; Nd(neodymium); microsttucture; mechanical property Magnesium alloy has been widely applied in various fields 1 Experlmental as one of the lightest structure materials because of its good performances[l]. AZ31 is a wrought magnesium alloy 也at is The AZ31 alloy containing Nd was prl叩ared by melting and widely applied for its excellent defonning property and satis- casting