场分布扫描套管腐蚀检测系统设计及实验探究.docVIP

场分布扫描套管腐蚀检测系统设计及实验探究 　　摘 要： 场分布扫描法是一种基于多频电流源激励下电流密度分布的套管在线腐蚀检测方法。设计场分布扫描套管腐蚀检测系统，为了初步验证场分布扫描法对腐蚀的可检测性，进行了穿孔实验。实验结果表明，场分布扫描法能够检测穿孔腐蚀，设计的电极系和检测系统对内直径为16.8 cm的金属套管上直径为6 mm的穿孔有较强的电敏感性 关键词： 场分布扫描法； 电流密度响应； 腐蚀检测系统； 腐蚀穿孔 中图分类号： TN02?34； P631.3 文献标识码： A 文章编号： 1004?373X（2017）09?0145?03 Abstract： The field distribution scanning method is a casing pipe online corrosion detection based on current density distribution excited with multi?frequency current source. A casing pipe corrosion detection system based on field distribution scanning was designed. To test the detectability of the field distribution scanning method to corrosion， a corrosion perforation experiment is carried out. The experiment result shows that the field distribution scanning method can detect the perforation corrosion， and the designed electrode array and detection system have strong electricity sensibility for the 6 mm perforation on a metallic casing pipe with 16.8 cm internal diameter. Keywords： field distribution scanning method； current density response； corrosion detection system； corrosion perforation 0 引 言 套管是油?饩?正常生产的重要保护屏障，套管腐蚀变形破损对油井的正常生产有至关重要的影响。套管损伤往往造成套管外串槽和漏失引发地层间串槽、注水能量分散等现象发生而引起采油效率降低和增产措施失效[1]。在美国，预计每年仅腐蚀造成的损失就达到了14亿美元；其中地面管线和设施损失为5.89亿美元，井下管柱损失4.63亿美元，资本支出3.2亿美元[2?3]。电磁检测法由于受管道内介质影响小，对管壁的光滑度要求不高，不但能发现管道各种异常，而且能测量管道的剩余壁厚等优点成为各国学者研究的热点[4?7] 文献[8?9]通过有限元仿真，发现当电流流过腐蚀区域时，均匀电流将受到扰动，使得电流场的分布发生改变；文献[10]研究了因腐蚀引起电流重新分配而导致测量电压的变化。基于此原理和套管建模仿真，本文提出了场分布扫描法（Field Distribution Scanning Method，FDSM）检测套管腐蚀[11?13] 1 场分布扫描套管腐蚀检测原理 场分布扫描法首先采用直流电流激励，向套管注入电流并使电流分布稳定，测量管道壁上的电流分布。若套管无腐蚀，则其管壁电阻分布均匀，径向电流密度相等，电流密度曲线将会重合；如果套管存在均匀腐蚀，电流密度会增大，电流密度曲线会平移后重合；如果套管存在非均匀腐蚀，套管介质的非均匀性变化会引起其管壁电流分布的非均匀性变化，管道壁径向各处电流密度不相等，电流密度曲线会发散。其数值反映腐蚀的严重程度，形态反映腐蚀形状和分布 其次改变激励电流频率，测出不同频率下测量电极间的电位差值，绘制电流密度曲线。根据曲线形态可判断腐蚀处于套管内壁还是外壁，综合多频激励电流下的电流密度曲线形态，进行软件聚焦和数据合成算法，能够将测量结果解释为3D图像 场分布扫描测量原理如图1所示 被测套管内部沿其长度方向依次设置与其内壁接触的激励电极A、测量电极C、测量电极D和激励电极B。由A和B向管道注入激励电流测量C和D之间的电位差测量电极C和D之间套管的电流密度δ可根据式（1）求得： 式中：V为C，D电极间的测量电位差；ρ为套管电阻