Full Paper 99 Summary: The powder blend of poly(acrylic acid) (PAA) those of the corresponding CAD data, was achieved. The with zinc oxide or zinc oxide/magnesium oxide was applied mechanical properties improved with increasing PAA con- successfully to produce zinc polycarboxylate during the 3D tent, ink amount (saturation value), decreasing particle size of dispensing of an aqueous ink by means of 3D printers thesinteredzincoxideceramic.AthighPAAcontent 7wt.-%, (Z402TM from ZCorporation and DeskmodelerTM from bmt post-treatment with aqueous zinc acetate solution improved Company). The layer-by-layer inkjet printing afforded zinc the mechanical properties. The setting time of the zinc ce- ionomer 3D objects with excellent water resistance, no inhe- ments shows no significant effect on the mechanical proper- rent color formation and high mechanical and dimensional ties, but on the water resistance of the models. The porosity of stabilities. In contrast to the 3D printing of conventional the 3D objects, measured by means of X-ray microtomo- powders such as starch/cellulose/dextrose blends, poly(vinyl graphy (m-CT), had profound impact on the variations of the alcohol) (PVA) or plaster, no postprinting treatments were mechanical properties of the 3D objects prepared by 3D required. Excellent dimensional accuracy of the models, as printing processes. evidenced by very small deviation of the dimensions from Comparison of three-point-bending tests of commercially available powders with selected zinc cements (ZC1, ZC2, ZC4, ZC19). Commercially available