熔融锌对热镀锌沉没辊的浸蚀机理及对策.pdfVIP

第2 卷 第1 期 热 喷 涂 技 术 Vol.2, No.1 2010 年3 月 Thermal Spray Technology Mar., 2010 熔融锌对热镀锌沉没辊的浸蚀机理及对策 樊自栓 （北京科技大学腐蚀与防护中心，北京 100083 ） 摘 要：简要综述了热镀锌带钢生产线沉没辊的工作情况及腐蚀机理，对国内外耐液锌腐蚀的材料以 及表面防护技术作了较为详细的介绍，指出热喷涂涂层可以有效地减缓锌的腐蚀，并且耐高温无机封 孔剂可大大提高热喷涂层耐液锌腐蚀性能，并提出了未来沉没辊耐液锌腐蚀的研究方向。 关键词：热镀锌；沉没辊；机理；表面技术；综述 中图分类号：TG174.442 文献标识码：A 文章编号：1674-7127 （2010 ）01-0001-07 The Mechanism and Countermeasure of Molten Zinc Corrosion of Sink Roll in Hot Dip Galvanizing Bath FAN Zi-shuan （Corrosion and Protection Center，University of Science and Technology ，Beijing 100083 ，China ） Abstract ：The working condition and mechanism of molten zinc corrosion of sink roll in hot dip galvanizing bath is analyzed. The material and surface treatment which can be used in molten zinc at present are introduced in detail. It is indicated that thermal spray coatings can reduce the corrosion from molten zinc，and sealing treatment by high temperature mineral sealing can improve the corrosion resistance to molten zinc. The research direction for protection of sink roll is pointed out. Keywords ：Hot-dipping galvanizing ；Sink roll；Mechanism ；Superficial technology；Review 目前世界各钢铁企业运行的带钢热浸镀机组 大都采用沉没辊装置，它主要由设置在锌液中的沉 没辊、稳定辊等组成，图1 所示为锌锅沉没辊工作 情况。沉没辊和两个稳定辊都完全沉浸在450～480 ℃的熔融锌液中，受到活性很强的锌液的腐蚀和渗 透，使辊面产生点蚀、蚀坑而变得粗糙，同时钢带 由辊面带动的运动速度高达35～40 m/s ，因此其工 作寿命一般都较短[1] 。 1 熔融锌对沉没辊的浸蚀机理 图1 连续镀锌生产线的锌锅沉没辊示意图[2] 在热浸镀锌槽中，钢铁与熔融锌扩散反应形成 多孔、疏松的低熔点锌渣（FeZn13 合金），并飘移 Fig.1 Sketch map of sink roll in in a zinc pot of a continuous galvanizing line[2] 作者简介：樊自栓（1964-），男，河南人，副教