高碳钢线材显微组织和屈服强度关系模型.docVIP

高碳钢线材显微组织和屈服强度关系模型 杨方敏，冯运莉，王成 (河北理工大学 金属材料工程系,河北 唐山　063009) 摘要：本文用光学显微镜和扫描电子显微镜，运用定量金相技术，分析计算了铁素体含量和珠光体片间距。研究了高碳钢线材的显微组织和屈服强度之间的关系，建立了表示两者之间关系的数学模型：σs（Pa）=×106+161.70（1－fα1/3）(m)。经验证，此模型与实验结果吻合得较好。 关键词：高碳钢，线材，显微组织，屈服强度，数学模型 Mathematical Model of The Relationship Between Microstructure and Yield Strength of High-Carbon Steel Wire FENG Yun-li, SHI-yan, WANG Cheng (Metal Material Engineering Department, Hebei Polytechnic University, Tangshan Hebei 063009, China) Abstract: Using Optical Microscope and Scanning Electron Microscope ,with the technology of fix quantity metallurgical phase, ferrite content and the plate distance of pearlite are analyzed. The relationship between the microstructure and yield strength of high carbon steel wire has been studied and the mathematical model of the relationship has been established : σs（Pa）=×106+161.70（1－fα1/3）(m).By examination，this mathematical model fits to the experiment result well. Key words: high carbon steel , wire ,microstructure ,yield strength , mathematical model 1 引言 高碳钢高速线材经深度拉拔可用于制造钢丝绳，弹簧钢丝，及汽车轮胎的帘线等，但国内的高碳钢高速线材在拉拔过程中极易拉断的问题亟待解决。这一质量问题除钢坯中夹杂物较多的影响外，主要取决于高速线材的生产工艺。为提高高碳钢线材的质量，应在开发高碳钢线材的性能预报方面进行深入的研究，即根据钢坯的化学成分和加工工艺参数，如钢坯的加热温度，开轧温度，形变温度，终轧温度，水冷段各个水箱的水压，风冷各段的风压等参数预报产品的性能，以实现产品的在线质量控制。试验研究表明，为了使高碳线材具有优良的拉拔性能,要求组织中的索氏体含量达到80%以上且均匀、细小，若索氏体化率偏低或出现其它异常组织,就会造成拉拔断或脆断现象。研究还表明高碳钢线材的屈服强度与钢中铁素体的百分含量，珠光体的片层间距等因素有关。因此为了实现准确预报，须建立显微组织与力学性能关系的数学模型。本文主要是对高碳钢线材的显微组织与屈服强度之间关系的数学模型进行研究，为高碳钢线材生产工艺的制定提供理论依据。 2 试验材料及方法 试验用钢取自唐钢产φ6.5mm的60号钢和65号钢，试样长度350mm，试验钢的化学成分见表1。用线切割机分别从每个试样上截取10mm长的圆柱形试样，以备金相检验之用，然后用SUN20电子拉伸试验机测试其力学性能见表2。 表1 试验用钢的化学成分（质量分数，%） Table 1 The chemical compositions of test steels（wt%） 牌号 C Mn Si S P 60 0.56 0.71 0.23 0.026 0.023 65 0.63 0.60 0.28 0.023 0.031 表2 试验用钢的力学性能 Table 2 The mechanical properties of test steels 试样号 σb/MPa σs/MPa δ10/% 60-1 939.76 834.28 12.86 60-2 934.61 806.78 14.28 65-1 1008.36 902.18 12.51 将上述金相试样磨光、抛光、用3%硝酸酒精溶液腐蚀后，用金相显微镜观测其组织，用定量金相的计点法测量了各试样中铁