激光处理钛合金表面和三元硬质涂层表面固体润滑涂层的滑动磨损特性.pdfVIP

Trans. Nonferrous Met. Soc. China 27(2017) 839−847 Sliding wear characteristics of solid lubricant coating on titanium alloy surface modified by laser texturing and ternary hard coatings M. PREM ANANTH, R. RAMESH Department of Mechanical Engineering, Sri Venkateswara College of Engineering, Sriperumbudur, Chennai-602117, Tamilnadu, India Received 22 March 2016; accepted 28 June 2016 Abstract: Titanium alloys are poor in wear resistance and it is not suitable under sliding conditions even with lubrication because of its severe adhesive wear tendency. The surface modifications through texturing and surface coating were used to enhance the surface properties of the titanium alloy substrate. Hard and wear resistant coatings such as TiAlN and AlCrN were applied over textured titanium alloy surfaces with chromium as interlayer. To improve the friction and wear resisting performance of hard coatings further, solid lubricant, molybdenum disulphide (MoS2), was deposited on dimples made over hard coatings. Unidirectional sliding wear tests were performed with pin on disc contact geometry, to evaluate the tribological performance of coated substrates. The tests were performed under three different normal loads for a period of 40 min at sliding velocity of 2 m/s. The tribological behaviours of multi-layer coatings such as coating structure, friction coefficient and specific wear rate were investigated and analyzed. The lower friction coefficient of approximately 0.1 was found at the early sliding stage, which reduces the material transfer and increases the wear life. Although, the friction coefficient increased to high values after MoS2 coating was partially removed, substr