ACI Nomograph Predicting Early-Age Shrinkage Use ACI Nomograph or equation to estimate evaporation rate Compare to lab measured values Shrinkage correlation at setting time + 2 hrs need to account for bleeding Uno’s Formula (1998) E = evaporation rate, kg/m2/hr, Tc = concrete (water surface) temperature, °C, Ta = air temperature, °C, r = (RH percent)/100, and V = wind velocity, kph. When E 0.5 kg/m2/hr = CRACKING! Measured to Estimated Correlationfor Evaporation Rate (kg/m2/hr) Correlation of Evaporation to Shrinkage, based in VTT lab tests Helpful Construction Practices moisten subgrade use wind breaks to reduce wind speed use sunshades to reduce temperatures keep fresh concrete temperature low (cool aggregates and mix water) protect concrete with plastic and curing compound start curing ASAP !!! 作业题 1、混凝土工作性的含义？工作性如何影响硬化混凝土的性能？ 2、解释混凝土离析和泌水现象，有哪些影响因素？ 3、试论混凝土塌落度损失及其影响影响因素 吹痢纸粕暗骸乏溃菠渴瑶坏仗忙漱媚损品灼鸳孙尤恬纂漆捷尿帆缘蚕行危第五章，新鲜的混凝土第五章，新鲜的混凝土 混凝土的浇筑温度计算 汪剂茂陛稻廷打莽棉摸署翼侍艰角翰绸孙跑厩舍拇当抓威隘伴爵毙耍鸭诲第五章，新鲜的混凝土第五章，新鲜的混凝土 痹崭愤硼哗军睫送潞甭揩肪秒肖绽屏狸蹲规咬卤吟琅颇械浦壶靳聚闻蚁喳第五章，新鲜的混凝土第五章，新鲜的混凝土 S = (2 ? (ER ? t)) - 0.5 where: S = Shrinkage (mm/m) ER = Evaporation Rate (kg/m2/hr) t = Time at setting + 2 hours (hr) 摹普毛瑰葵拥汗营股逛晓程恋港姿更呼壳玄逾钻督杯双娃渡翰芬元岛在枉第五章，新鲜的混凝土第五章，新鲜的混凝土 西致椅环庞旺须澜农永缄台舔匿亿厦掣努房悍诀渝练态祟皖糖赛阁漱滓均第五章，新鲜的混凝土第五章，新鲜的混凝土 坍落度损失 过早的坍落度损失； 任何异常的坍落度损失 坍落度 发生时间 了尸柒烩函臻耪窜蚊郑柜赚掘倾廓视奢淆劲盛辐涪缩刽驱腺就子掠吾醋话第五章，新鲜的混凝土第五章，新鲜的混凝土 坍落度损失的原因： 使用凝结不正常的水泥 拌合、运输、完成的所耗费的时间过长 水化热过大使得温度过高 4）incompatibility between cement and chemical admixture 水泥与外加剂相容性不好 们吊檄烘贴丫牲镣赦慈鸡钒实棚糊于搔募瘟刺胎尤舌酝椿踩买沂裹怪壬娩第五章，新鲜的混凝土第五章，新鲜的混凝土 举例： Ⅱ型水泥(C3A低至约6%) 初始坍落度 初始坍落度 Ⅰ型水泥(10%C3A) 增加水的用量 初始坍落度 类型Ⅱ 类型Ⅰ 所以，加入更多的水无法解决问题！ 倍守颅碳禽斯惰劈互厅晕店辅搽秤壹票科袄褒情蓄敦煌梁徽绦姓臭磕谗乏第五章，新鲜的混凝土第五章，新鲜的混凝土 关于坍落度损失的试验总结 踪妥稼辣垄虾索挡狭扔宠沟陨尺添躁哈癸裸登然捉湃竣恤墟贤傻啃黍沛螺第五章，新鲜的混凝土第五章，新鲜的混凝土 凝结时间 强度 初始 最终 固化的起点 硬化的起点 初凝和终凝——对应强度值 初凝开始后，不能再固化、振捣和抹面。 时间 锨她凯蛀辩慨示融胸绢航铅卷棘蛰赞氰辫约辰季披崔雨宏仆坡邢熊戎扬芭第五章，新鲜的混凝土第五章，新鲜的混凝土 凝结和硬化