材料分析技术(示波冲击试验).ppt

（3）Energy to Yield Energy to yield is the energy that the specimen has absorbed up to the point of yield. It is the area under the load/deflection curve from the test start to the yield point. （4）Energy to Failure Energy to failure is the energy that the specimen has absorbed up to the point of specimen failure. It is the area under the load/deflection curve from the test start to the failure point. （5）Total Energy Total energy is is the energy that the specimen has absorbed up to the end of the test, when the load reaches zero again. It is the area under the load/deflection curve from the test start to the test end. （4）其它特征值 以上特征参数软件均可给出，也可以通过自己设置的公式显示软没有的特征参数，如冲击韧度ak。 (2) 　各种能量指标的确定 关于裂纹形成能量及裂纹扩展能量,理论上认为裂纹在最大力时形成。当冲击力达到最大力时,裂纹在冲击试验缺口处形成,因此把冲击最大力作为裂纹形成的依据: 最大力之前所消耗的能量称为裂纹形成能量——裂纹萌生功Wi : 力—位移曲线下,从S = 0 到S = S m的面积,即Wi≈ Wm ; 最大力之后所消耗的能量称为裂纹扩展能量——裂纹扩展功Wp： 力—位移曲线下,从S = S m 到S = S t 的面积,即Wp = Wt- Wi。 为了便于分析,将力—位移曲线下的面积,以力特征值为界分为5 个部分,称为基本能量单元: （1）We:弹性变形功 （2）Wd：弹塑性变形功 （3）WPl裂纹稳态扩展功 （4）WP3裂纹撕裂能量 （5）WP2裂纹剩余扩展功 标准中给出的能量由上述5 个部分组成: 裂纹萌生功 Wi Wi= Wm = We + Wd 不稳定裂纹扩展起始能量Wiu Wiu = We + Wd + Wp1 = Wi + Wp1 不稳定裂纹扩展终止能量Wa Wa = We + Wd + Wp1 + Wp3 = Wi + Wp1 + Wp3 裂纹扩展功Wp ： Wp = 稳态扩展功（Wp1）+ 失稳扩展功（Wp2 + Wp3） 总冲击能量Wt ： Wt = We + Wd + Wp1 + Wp2 + Wp3 = Wi + Wp （3）能量特征值的应用实例 对于不同材料，其冲击功Wt可能相等，但是它们的弹性变形功We、塑性变形功Wd及裂纹扩展功Wp所占的比例相差可能很大，从而表现出它们之间的韧脆性不同。 冲击力一位移曲线可以反映出它们在冲击性能上的差异。 材料1： 弹性功所占的比例很大，塑性变形功很小，裂纹扩展功几乎为零。 说明材料断裂前塑性变形很小，裂纹一旦形成，就立即扩展直至断裂，显示出材料的脆性。 材料2：弹性变形功比前者小，塑性变形功增加，裂纹扩展功也有一定的增加，当裂纹发展到一定尺寸时产生失稳扩展，表现出材料的半脆性性质。 材料3：弹性变形功较小，塑性变形功增加，裂纹产生后发生缓慢地扩展，直至断裂也不存在失稳，充分显示出材料具有很好的韧性性质。 3)示波冲击试验的应用前景 （1）表面强化效应的研究。 由于冲击时试样缺口截面上受力是不均匀的，缺口处受拉应力，缺口根部拉力最大。如果缺口表面状态有变化，例如喷丸、镀层、滚压或者渗碳等均会使表面强化并且产生压应力，而腐蚀会使表面弱化，那么冲击试验对其强化或弱化效果会很敏感，使冲击力或者冲击能量增加或减少。 （2） 对冶金质量及热处理工艺缺陷进行定量检验。 把具有使用价值的冲击力、位移、裂纹形成功及扩展功等冲击性能，作为检验依据以评定缺陷的严重程度，分析其形成原因。 （3） 对材料的韧脆转变的评估。因为裂纹扩展功在转变过程中变化显著，不仅能够给出定量评估指标，而且能从微观形态和宏观断口上进行分析。 （4）材料的韧脆程度将会以韧性断面率来衡量。同一种材料不同状态的韧性断面率可以进行比较。 （5） 宏观断口与所测出的冲击力或冲击功参数之间的研究，会使您