某超临界机组高温过热器爆管原因分析与预防 - bowen publishing.pdf

April 2013, Volume 2, Issue 2, PP. 56-62 Energy Development Frontier 某超临界机组高温过热器爆管原因分析与预防 1, 2 2 *1 王瑞民 ，张首会 ，谢学军 1. 武汉大学，湖北 武汉 430072 2. 襄阳电厂，湖北 襄阳 441141 摘 要：本文介绍了某电厂一台600 MW 超临界机组自2007 年投运以来发生的3 次过热器爆管情况。结合检查、处理过程，从 设计、运行、金属材质和氧化皮的测量数据等方面对爆管原因进行了分析，并从理论上分析了氧化皮的产生剥落机理。针对该 厂实际情况提出了相应的预防措施，取得了较好成效，可供同类型机组的运行和维修人员参考。 关键词：超临界机组；过热器；爆管 Explosion Reason Analysis and Prevention of a High Temperature Superheater in a Supercritical Unit Ruimin Wang 1, a, Shouhui Zhang2, b, Xuejun Xie *1, c 1. Wuhan University, Wuhan, China, 430072 2. Xiangyang Power Plant, Xiangyang, China, 441141 a b *c mrwxxx@163.com; zhangshh@; xiexuejun@163.com Abstract: The boiler tube burst of a 600 MW supercritical unit in a power plant was described. The tube burst reason was analyzed in detail. And the effective treating and preventing measures were presented, which could be used as the reference of the operation and maintenance personnel of the similar units. Keywords: Supercritical Unit; Superheater; Boiler Tube Bursting 1 概述 某电厂2×600 MW 超临界机组（#5、#6 机组）选用的是上海锅炉厂设计制造的SG1913-25.4-M947 锅炉，为 超临界参数变压运行螺旋管圈直流炉，是单炉膛、一次中间再热、四角切圆燃烧方式、平衡通风、Π 型露天布 置、固态排渣、全钢架悬吊结构。 锅炉过热器采用无缝合金钢管，管径较细；材质为SA-213 T23、SA-213 T91、SA-213 TP347H等。高温区域 使用的管材，除要求有一定强度、抗高温性能外，还要求管内外壁有很好的抗氧化性能，特别是超临界机组的 [1] 管材内壁要求有很好的抗蒸汽氧化性能 。高温过热器每排管圈数与蒸汽及烟气流速有关，锅炉高温过热器设计 蒸汽流速小于12 m/s，压降为0.3 MPa 。过热器中烟气流速综合考虑传热性能、积灰和飞灰磨损三方面因素，采 用11.8 m/s左右，不允许高于14 m/s[2] 。过热器管组的有关数据如表1。