环氧树脂特种固化剂的研制与应用（Development and application of epoxy resin special curing agent）.docVIP

环氧树脂特种固化剂的研制与应用（Development and application of epoxy resin special curing agent） Development and application of epoxy resin special curing agent Liu shougui tan zhou qin zhang jie (zhonghao chenguang chemical research institute sichuan zigong 643201) Abstract: this paper introduces a special synthesis method and application of epoxy resin curing agent which can be used for oil surface, underwater and low temperature curing. Keywords: synthetic application of epoxy resins 1. The introduction The products of epoxy resin are being serialized, refined, colorless, specialized, high purification, green and environmental-friendly, and cost-effective. The supporting agent products are forming scale, high purification, specialisation, high sexual energy and specialization. A new kind of epoxy resin curing agent is developed to provide an excellent curing performance, which is equal to the new application of epoxy resin. In fact, its much easier to develop a new type of epoxy resin than to develop a new type of epoxy resin. For certain curing defects existing in existing curing agent, [1] can be obtained by improving the raw material variety, formulation or new synthetic process route. The special curing agent used in special environment (wet, underwater, outdoor cold environment etc.) is popular. With the construction of water conservancy projects in China, the defect of reservoir dam has been repaired, and the underwater engineering has been closed and leakproof, so a kind of hardener can be applied underwater. For various reasons, it is impossible to clean up the oil thoroughly, and urgently need a curing agent that can be glued together. The winter outdoor anticorrosive construction in the northern region requires that the curing system of epoxy resin have good cold curing properties. The patent [2] reports a synthesis of a rapid curing agent of mannioid in low temperature, humidity and other special conditions. However, there is a defect of brittleness and low strength.