蜜胺树脂（Melamine resin） Formula of melamine formaldehyde resin Reward points: 5-14 days and 22 hours before the end of the problem Main agent: melamine 100 water 45 formaldehyde 193 6 submethylene tetramine 3.3 polyvinyl alcohol 5 Modifier: ethanol 98 water 57 (above all for quality) Regulator: sodium hydroxide triethanolamine right amount Whether this statement is true or not can be explained in detail The research status of modified melamine resin and its main application Melamine and melamine, which is an important kind of nitrogen heterocyclic chemical raw materials, as the main raw material synthesis of melamine resin (MF) has high reactivity, has been widely used in wood, plastic, paint, paper making, textile, leather and other fields. In order to satisfy the requirement of melamine resin in different application fields, it must be modified. The modification methods of melamine resin in various applications are reviewed. The synthesis of melamine resins Melamine resin and melamine formaldehyde resin (MF), usually by melamine and formaldehyde in neutral or slightly alkaline conditions after hydroxymethyl im into various methylol melamine, because of melamine has six faculties, so often get the reaction process is a combination of a variety of adduct. The thermosetting amino resins were produced by condensation of the derivatives of hydroxymethyl groups under the microacidic condition (pH 5.5 to 6.5). Melamine formaldehyde tent purport of reaction temperature, melamine/formaldehyde amount of substance ratio and the influence of factors such as pH, solid content, and with the increase of reaction temperature, formaldehyde content increases, the dissolution of melamine, reaction speed is quickened significantly. In the study of hydroxymethyl addition reaction kinetics, Gordon found that the active hydrogen of amino (-nh2) and subamino (-nh2) was different from that of formaldehyde, and the amino group was weak and the amino group was stronger. Braun also studied the