23MnNiMoCr54链条钢焊接断裂原因分析.DOC

23MnNiMoCr54链条钢焊接断裂原因分析 赵亚娟 田力(南京钢铁股份有限公司，南京 210035)ZHAO Ya-juan TAO Tao TIAN Li (Technology Quality Department of Nanjing iron and Steel Co. Ltd, Nanjing 210035,Jiangsu,China) Abstract: 23MnNiMoCr54 ?chain steel fractured in the weld joints in use processing, the?fracture?phenomenon was detailed analyzed in the paper, using spectrometer,?oxygen nitrogen analyzer,?scanning electron microscope and?electron probe?instrument to study, results show that, the chemical composition,?sample?analysis of the low magnifications, hardness?can meet the national standard requirements, ?the fracture occurred in the?weld,?the?foreign Cu?into the?lead to?grain boundaries, and grain boundary?strength decrease sharply,?leading to fracture, so occurrence of?welded joints?for?welding process,?should?strictly regulate?controlled to improve?the quality of?weld. Key words: chain steel of 23MnNiMoCr54，welding，hot brittleness of Cu 前言 23MnNiMoCr54链条钢具有高强度、高韧性，良好的耐疲劳性和冷弯性能，在我国矿业、重型运输机械等行业广泛应用。其中焊接作为圆环链生产的关键工序之一，由于闪光对焊方法具有省时、省料、省能源等诸多优点而常常被采用[1-3]。但如果焊接工艺控制不当容易日后使用过程中发生断裂等问题。最近，某厂生产的23MnNiMoCr54链条钢在用户的使用过程中，个别试样从焊缝接头处发生断裂，为此，本文从多方面进行了系统的分析，以找出断裂的原因。 作者简介：赵亚娟（1980—），女，硕士研究生，高级工程师；E-mail：zhaoyajuan@； 联系电话 无基金项目 1 试验与分析 焊接试样的链条钢生产工艺为：坯料验收→步进炉钢坯加热→高压水除鳞→粗轧→1#飞剪→中轧→2#飞剪→精轧→3#飞剪→冷床冷却→定尺剪切→缓冷→退火→矫直→剥皮或酸洗修磨→探伤→成品检验→包装→标识→称重→入库开轧温度目标值为1100±40℃，终轧温度950~1000℃，C Mn P S Si Ni Cr Cu Alt Nb Mo 0.226 1.204 0.008 0.003 0.15 1.02 0.52 0.07 0.024 0.002 0.553 V Ti B Ca As Pb Sn Sb Bi O(PPM) N(PPM) 0.003 0.001 0.0003 0.0010 0.004 0.0001 0.005 0.002 0.0006 ≤10 27 1.2 酸洗低倍分析 对断口附近进行横向截取，进行1:1工业盐酸热酸洗实验，加热温度75℃，加热时间约半小时，低倍结果用相机拍摄如下图，评级结果如下表，均小于1.5级，在合格范围之内。 图1 试样的宏观低倍图 Figue. 1 Macro graph of the sample 表2 试样的低倍评级结果 Table. 2 The ratings of the low magnification 低倍缺陷类型 一般疏松 中心疏松 锭型偏析 级别 1.0级 0.5级 0级 1.3 硬度分析 对试样横截面进行九点布氏硬度测量，硬度值如下表，硬度整体较均匀。 表3 试样的布氏硬度值 Table. 3 Brinell?hardness?of the sample 硬度位置点 1 2 3 4 5 6 7 8 9 平均 数值 213 218 211 212 198 204 212 205 194 207 1.4 扫描电镜分析 对试样断口用JSM-6