La-Co置换对锶铁氧体结构和性能的影响 Effect of La-Co substitution on the microstructure and properties of Sr-ferrite.pdfVIP

工艺·技术·应用 La-Co 置换对锶铁氧体结构和性能的影响 刘 辉，徐文生，谢光环，熊凌云 （北矿磁材科技股份有限公司，北京 100070 ） 摘 要：主要讨论La-Co 置换各向异性烧结铁氧体在磁性能上的改善。M 型烧结铁氧体中用La3+置换Sr2+ ， Co2+ 置换 Fe3+ ，有效提高了烧结磁体的饱和磁化强度以及磁晶各向异性场，获得优异的磁体磁性能为：剩磁 3 B =435mT 、矫顽力H =318.5kA/m 、内禀矫顽力H =366kA/m 、最大磁能积(BH) =36.0kJ/m 。 r cb cj max 关键词：锶铁氧体；La-Co 替代；结构；磁性能 中图分类号：TM277+ .2 文献标识码：A 文章编号：1001-3830(2013)05-0063-04 Effect of La-Co substitution on the microstructure and properties of Sr-ferrite LIU Hui, XU Wen-sheng, XIE Guang-huan, XIONG Ling-yun BGRIMM Magnetic Materials Technology Co, Ltd, Beijing 100070, China Abstract: In this paper, the improvement of magnetic properties of anisotropic sintered ferrite with La-Co substitution was researched. The saturation magnetization and magnetocrystalline anisotropy field have been significantly improved by partial substitution of Co2+ and La3+ ion for Fe3+ and Sr2+ ion respectively in M-type sintered ferrite. Magnet was obtained with magnetic properties as follows: remanence Br=435mT, coercivity Hcb=318.5kA/m, 3 intrinsic coercivity Hcj =366kA/m, and (BH)max=36.0kJ/m . Key words: Sr-ferrite; La-Co substitution; microstructure; magnetic properties Sr － La O·n(Fe － Co ) O ，n=5.4~6.3 1 引言 1 x x 1 y y 2 3 其中x 和y 分别表示发生替代的La3+和Co2+ 的离子 近年来，随着绿色经济和节能环保产业的不断 数，x=y ，n 是Fe [3]