Heat Treatment of Steel Sacramento State（钢的热处理,萨克拉门托的状态）.pdf

              Heat Treatment of Steel Engineering 45 Materials Monday 8:00 AM Lab Troy Topping 10/31/11 Deanna Becker 11/21/11 Abstract This procedure compared properties of heat treated 4140 steels and accurately represented processes that material science engineers use in design. Two specimens of 0.505- inch-diameter 4140 AR steel were heat treated into the quenched and tempered state and hardness and tensile tests were performed. From the stress-strain curves created, the elastic modulus, the 0.2% offset YS, the UTS, the % elongation, and the % reduction for samples on samples A and B were as follows respectively: 33,866 ksi and 29,162 ksi; 166 ksi and 168 ksi; 180,325 psi and 186,940 psi; 11.30% and 15.19%; and 36.03% and 37.46%. The hardnesses in the as quenched state on the Rockwell C scale for samples A and B were determined to be 47.7 and 47.3 respectively. The hardnesses in the quenched and tempered state on the Rockwell C scale for samples A and B were determined to be 31.9 and 33.4 respectively. Also, two specimens of 0.505-inch-diameter 4140 AR steel were heat treated into the fully annealed state and hardness and tensile tests were performed. From the stress-strain curves created, the elastic modulus, the 0.2% offset YS, the UTS, the % elongation, and the % reduction for samples on samples A and B were as follows respectively: 27,