一种海绵状伤口敷料制备及结构性能探究.doc

一种海绵状伤口敷料制备及结构性能探究摘要：采用冷冻壳聚糖-明胶共混液诱导相分离的方法，制成多孔性、亲水性、透气性良好的海绵状伤口敷料。通过对海绵体敷料结构及性能的研究，结果表明：壳聚糖与明胶分子之间形成了较强的氢键，壳聚糖中的-NH2与明胶中的-COOH发生酰胺化反应，说明壳聚糖的羟基与交联剂之间有反应发生，其反应历程有待进一步研究。由此可认为两种物质达到分子水平的分散，具有良好的相容性。 关键词：壳聚糖；明胶；相分离；海绵状伤口敷料 [Abstract] By freezing chitosan-gelatin complex induce phasic abruption, the porous and ventilative spong of chitosan-gelatin was made, and the spong of chitosan-gelatin was studied on its structure and performance. The result indicated that: There were strong hydrogen bonds formed between the molecules of chitosan and gelatin. The amidation reacted in -NH2 of chitosan and ?OOH of gelatin.Moreover, thechitosan Has Condensation reaction with the crosslinking agent . According to the above elaboration may think two kind of matter achieved the molecular level the disperser, they has the good compatibility. [Keywords]Chitosan, Gelatin， Phasic abruption，Sponge of wound dressing 甲壳素又名甲壳质、几丁质，大量存在于虾、蟹等海洋节肢动物的甲壳中，也存在于低等动物菌类、昆虫、藻类的细胞膜和高等植物的细胞壁中，分布极其广泛，壳聚糖是甲壳素经乙酰基反应后得到的可溶性物质，由于其具有良好的生物相容性、生物可降解性，和良好的成膜性、抗凝血性、促进伤口愈合和防腐抗菌等功能，作为医用材料备受关注；明胶是动物胶原经温和断裂后的产物，主要成份是胶原、少量的蛋白多糖及某些有机成份。胶原能参与细胞的迁移、分化和增殖，使骨、腱、软骨和皮肤具有一定的机械强度。因其弱的抗原性和良好的生物相容性，在烧伤、创伤、眼角膜疾病、美容、矫形、硬组织修复、创面止血等医药卫生领域用途广泛[1-5]。 目前技术中，有文献报道了一种将壳聚糖溶液冷冻制备高孔隙率膜的方法[6]。也有一些壳聚糖-明胶止血海绵、膜或敷料的研制方法[7]。本研究使用壳聚糖、明胶二者复合，利用各自优点，并且在其中加入具有清热解毒、杀菌消炎、止血生肌、去翳明目等功效的珍珠粉。既可以增加药效，又可以中和醋酸的酸性，还可以使水的晶片变得细小和均匀，从而形成具有独特的膜孔结构的海绵状材料。 1 实验部分 1.1原料及设备 原料：壳聚糖（由湛江产海水养殖虾虾壳自制）脱乙酰度97.55%，=1.85×106 ；明胶CP.级，上海化学试剂分装厂、 冰乙酸、NaOH、甲醛、甘油,均为CP级。 设备：XL30-EDAX扫描电子显微镜（荷兰Philips 生产）；3365型万能材料试验机；Nicolet-550型红外光谱仪 1.2 壳聚糖-明胶海绵伤口敷料的制备 1.2.1 壳聚糖溶液的配制壳聚糖溶解于1.5%冰乙酸水溶液中配制成2~3%的溶液，室温下搅拌至完全溶解,静置过夜。 1.2.2 明胶处理 明胶以3%质量分数在蒸馏水中浸泡，水浴加热溶解，搅拌后离心， 去除沉淀。 1.2.3混合液的配制 将壳聚糖溶液分别与明胶溶液以壳聚糖/明胶= 4:1~1:4（质量比）等不同比例混合混合，静置脱泡； 1.2.4交联 分别移取一定量不同比例的混合液，加入1/15~1/10（质量比）的珍珠粉，配入少量交联剂及致孔剂聚乙二醇，静置脱泡，低温下淬冷、固化，取出用蒸馏水冲洗表面至pH值≈6，用滤纸吸干水份，风干至湿度≈15%，经消毒后备用。为增强产品的机械强度，在所配制的溶液中加入重量比为0.1~0.5%甘油或乙二醇作为增塑剂。 1.3 用扫描电镜观察表面结构与截面结构 将样品按常规方法镀金,在扫描电镜上进行观察。 1.4红外光谱 在N