探究热拌沥青混合料路面早期损坏原因.docVIP

探究热拌沥青混合料路面早期损坏原因摘要：沥青混凝土路面具有无接缝、表面平整性好、舒适性强、造价相对较低、行车舒适、修复方便，能够利用石化企业副产品等优点而被广泛用于公路和城市道路、机场等基础设施的路面层处理。其主要类型有沥青表面处治、沥青贯入式、热拌沥青混合料和乳化沥青混合料路面等，但也因为具有热拌沥青混合料路面的所属特性，有早期损坏严重的工程质量通病，如：泛油、波浪、壅包、滑溜、裂缝、坑槽、局部沉陷、松散、车辙等。本文针对热拌沥青混合料路面早期损坏的质量通病作浅析。 关键词：热拌沥青混合料； 路面施工；早期损坏； 分析原因；对策措施 Abstract: the asphalt concrete pavement has no juncture, the surface is the gender is good, comfort, relatively low cost of strong, driving comfort, repair and is convenient for using petrochemical enterprise by-products of advantage and is widely used in highway and city roads, airports and other infrastructure road surface layer of processing. The main types of asphalt, asphalt surface will have penetration type, hot mix asphalt mixture emulsified asphalt mixture and road and so on, but also because have hot mix asphalt mixture of pavement subordinate characteristics, there are early damage of serious engineering quality problems, such as: the oil, and the waves, warm bag, gliding, crack, pit slot, local subsidence, loose, rutting, etc. This article in view of the hot mix asphalt mixture the quality of the road surface early damage the super analysed. Keywords: hot mix asphalt mixture; Pavement construction; Early damage; The causes; countermeasures 中图分类号： U415 文献标识码： A 文章编号： 近年来，连云港市作为沿海城市的开放力度加大，城市改造的步伐加快，市政基础设施投入力度大，修建了许多城市主干道及支路，而一些道路的沥青混合料路面面层在不同程度上均出现了早期损害，严重影响了道路的使用性能及耐久性，并制约了经济的发展。为了提高沥青路面的施工水平，笔者根据多年市政道路工程的施工经验，较科学地分析沥青面层早期损害的原因，并针对原因，采取合理的有效措施，切实贯彻落实到沥青路面管理、监理、施工及设计过程中。 一、沥青路面病害的现场调查和检测分析 根据对城市道路的现场观察和统计，由于交通量及荷载的不同，城市道路病害程度和形式也各不相同，总的来说，具有以下一些特点：①快车道、正常行车道损坏要严重；②交通量大、重型车辆多的损坏要严重；③表面油污染重、平整度差的损坏要严重；④温差大、积水多的地区损坏要严重。 1.1路面表观调查 为科学客观地分析沥青路面早期损害的原因，并针对性地提出改进措施，表面实地调查是一项非常重要的工作。通过大量观察及调查，早期损坏的类型可归结为：车辙、裂缝、松散、剥落、坑塘、壅包、泛油、推挤和表面磨损等表现形式。 1.2钻孔取芯检验 为获取沥青路面损坏程度的量化数据，分析路面病害产生的真正原因，钻孔取芯同样也是一项非常重要的具体工作。现选出具有代表性的一段，见表1。 表1钻孔取芯检测表 通过大量的钻孔取芯试样观察及压实度、抽提、马歇尔试验、构造深度等试验检测情况来看，凡出现病害的严重路段，均存在以下主要问题： 1.3 沥青混凝土面层厚度偏差太大，严重不均匀； 1.4沥青混凝土路面面层所用的石灰岩骨料中，含有产生锈斑的烂石料，或呈粉状的石