浅议钢筋混凝土裂缝问题摘要:混凝土的裂缝问题是一个普遍存在而又难于解决的工程实际问题，由于裂缝的存在和发展通常会使内部的钢筋等材料产生腐蚀，降低钢筋混凝土材料的承载能力、耐久性及抗渗能力，影响建筑物的外观、使用寿命等。人们对建筑质量的要求日趋严格，在这种建筑形势下工程结构的裂缝问题变得日趋突出。因此如何解决这种常见的混凝土裂缝，是设计者和施工者都不可忽视的问题。 Abstract: the concrete crack is a widespread and difficult to solve engineering problems, due to the existence and development of cracks will usually reinforced materials such as the internal corrosive, reduce the carrying capacity of reinforced concrete materials, the durability and anti-permeability ability, affect the appearance of the building, service life etc. People to the requirements of the quality of the construction strictly, in the construction situation of engineering structure crack problem getting more outstanding. Therefore, how to solve this kind of common concrete crack, is the designer and all kinds of problems that cannot be ignored. 中图分类号： TV543 文献标识码： A 文章编号： 一混凝土产生裂缝的原因 混凝土裂缝的产生,都是微裂缝发展的结果。就其本身而言,一般认为是混凝土材料变形约束所引起的内应力大于材料抗拉强度所致。 1 材料方面的原因1.1 材料方面的原因材料选配不当形成缺陷和裂缝。使用过期水泥,骨料含泥过量,含活性SiO2,水泥中含碱量过高,骨料石灰石,水泥水化热等。 其次砼原材料性能缺陷是裂缝的主要诱因之一。建筑工程钢筋砼构件中有大约80%的裂缝不是经由外荷载作用引起，而是在砼浇筑后不久或在施工阶段尚未承受外荷载之前就已开裂。这是由砼材料本身变形引起的，其重要的影响因素有：环境因素（即温差及湿度）、收缩、膨胀、徐变、塑性坍塌、不均匀沉降等。其中环境因素和收缩是造成裂缝的最主要原因。 （1）因环境因素影响形成缺陷和裂缝。主要是温度和湿度的变化,混凝土的脆性和不均匀性,以及结构不合理,原材料不合格(如碱骨料反应),模板变形,基础不均匀沉降等。混凝土构件多次受冰冻,即溶解循环作用,使混凝土中产生内应力,促进已有裂缝发展,结构疏松,表面龟裂,表层剥落或整体崩溃。 水泥水化是个放热过程。砼在硬化过程中水泥放出大量的水化热，使得砼结构内外出现较大的温差，这些温差造成其内外部热胀冷缩程度不同，使砼表面产生一定的拉应力。同样，砼在后期降温过程中，也会在内部出现拉应力。 （2）收缩裂缝。砼是一种收缩性材料，在砼浇筑后水泥出现硬化，水分急剧蒸发，砼体积急剧收缩，收缩变形也会产生拉应力。而此时的砼早期强度低，不能抵抗这种变形，当拉应力大于其抗拉强度时，易引起干燥收缩裂缝和塑性收缩裂缝。1.2 施工操作的原因 施工违反操作规程形成缺陷和裂缝。塑性混凝土下沉,被顶部钢筋所阻,形成沿钢筋的裂缝;混凝土振捣不密实,出现蜂窝,易形成各种受力裂缝的起点;混凝土初期养护时急剧干燥使得在混凝土与大气接触面上出现不规则的网状裂缝;过早拆模,混凝土尚未建立足够强度,构件在实际施加与自身的重力荷载作用下,容易发生各种受力裂缝等。其中砼的影响因素尤为突出 （1）砼振捣不均匀、不密实。在浇捣过程中振捣不充分或者振捣过度，会造成砼的密实度不均匀，密实度大与密实度小的砼体产生不同的拉应力，容易产生裂缝。（2）砼拆模过早、构件起吊过早或加载过早。拆模过早时，砼未达到规定强度会导致表面开裂；构件起吊过早或加载过早会发生垂直于主筋的横向裂缝。（3）养护不到位。砼养护十分重要，但许多施工单位却忽视这一环节，特别是由于保温保湿养护不到位，导致温差裂缝和干缩裂缝产生。 1.3 设计方面的原因 设计人员对建筑中易产生裂缝的部位，往往没有进行单独考虑，并有针对性的提出防裂要求和具体措施。例