丙乳砂浆在马山闸除险加固工程中应用.doc

丙乳砂浆在马山闸除险加固工程中应用 摘要：丙乳砂浆是一种新型混凝土建筑物的修补材料，具有优异的粘结、抗裂、防水、防氯离子渗透、耐磨、耐老化等性能，和树脂基修补材料相比具有成本低、耐老化、易操作、施工工艺简单及质量容易保证等优点。本文结合实际案例，对该项技术的施工工艺及应注意的问题作了介绍。 关键词：丙乳砂浆 ，马山闸 ，水闸加固 ，施工工艺 ，应用 Abstract: the acrylic mortar is a new kind of concrete building repair material, has excellent bonding, crack, waterproof, prevent chloride permeability, wear resistance, ageing resistance, such as performance, and resin matrix material than repair with lower cost, ageing resistance, easy to operate, the construction technology and quality easy to ensure that simple, etc. This paper combining with actual cases, the technology and the construction technology of the problems that should be paid attention to are introduced. Key words: the acrylic mortar, mashan brake, locks reinforcement, construction technology, the application 中图分类号：K826.16文献标识码：A 文章编号： 一、工程概况 马山闸位于绍兴县孙端镇曹娥江出口左岸侧，即在曹娥江下游，紧靠江边，水闸中心线与曹娥江河道中心线呈50°相交。工程为Ⅲ等水利工程（闸门Ⅱ等），防洪标准按五十年一遇标准设计，百年一遇标准校核，原设计平均过闸流量为320m3/s。全闸共分6孔，每孔高6m，净宽8m，闸孔总净宽48m。2009年1月，在浙江省水利厅的组织下根据《水闸安全鉴定规定》（SL214-98），对绍兴县马山闸进行了安全鉴定。鉴定结论：马山闸运行已长达45年，其防洪标准、闸基抗渗稳定性、水闸排涝过流能力、启闭力仍能满足规范要求。但部分混凝土构件、电气设备等都存在着不同程度的老化和破坏：启闭机大梁不满足规范使用状态极限要求；胸墙、砼闸门、公路桥等混凝土胀裂、钢筋锈蚀；闸墩、翼墙伸缩缝错开；翼墙部分位置破损严重、产生倾斜；下游左右岸护坡开裂、倒塌、破损严重，弧形钢闸门和钢筋砼工作闸门金属构件及埋件锈蚀严重，滚轮锈死，止水橡皮老化破损、漏水严重。电气控制系统比较落后，且设备陈旧、老化，工作不可靠等问题将影响闸门的正常安全运行，评定马山闸工程为三类闸。 二、丙乳砂浆修补加固范围的确定 根据安全鉴定的结论确定修补加固的范围：各孔闸墩在水位变化区、各孔钢筋砼闸门局部、各孔胸墙局部、立柱混凝土中钢筋局部位置、启闭便桥桥面、启闭机大梁底面、交通桥及两侧引桥桥面铺装层、上下游左、右岸翼墙混凝土在在水位变化区局部混凝土剥落，石子裸露严重。 三、聚合物水泥砂浆的比选 根据本工程的特点，适合本工程的聚合物砂浆主要有：丙乳砂浆、氯丁砂浆和丁苯砂浆。 丙烯酸酯共聚乳液、阳离子氯丁胶乳和羧基丁苯乳液均为高分子聚合物的水分散体，加入水泥、砂中拌和后成为聚合物水泥砂浆。它们均具有聚合物水泥砂浆的共同特性，即与老混凝土粘结良好、抗裂、抗冻、防渗、防腐、抗氯离子渗透、耐磨、耐老化等性能，适用于水利、港口工程、公路、桥梁、冶金、化工、工业与民用建筑等钢结构和钢筋混凝土结构的防渗、防腐护面和修补工程。但这三种乳液分属不同类型热塑性材料乳化而成，因此各有优缺点，针对本工程分析如下： ①丁苯水泥砂浆虽然抗压强度较高，但由于其固化较快，表面失水后若未及时洒水养护，极易引起开裂、脱空，对施工养护的要求高，因此不推荐用于户外大面积使用。该材料较适合用于各类涵洞的抗冲、防渗护面。 ②氯丁水泥砂浆粘接性能优异，且由于是橡胶改性的乳液，具有一定的韧性，在三种材料中其抗裂性能特别突出，对养护条件的要求也低于其它两者，因此适用于对粘接、抗裂有较高要求及养护较困难的场合。但需采用人工拌合，若机械拌合易产生大量气泡。 ③丙乳水泥砂浆强度介于丁苯水泥砂浆和氯丁水泥砂浆之间，与新老混凝