浅议水利工程钢结构防腐施工技术.docVIP

浅议水利工程钢结构防腐施工技术【摘 要】：随着我国国民经济的飞速发展,国家对水利基础建设投入也不断加大,水工建筑物的设计标准和规模也越来越高。钢结构在涵闸工程中大量运用,随之而来,钢结构的腐蚀问题也越来越突出。文章从钢设备的腐蚀原理以及防护策略、金属热喷涂的工艺基础等方面介绍了水利工程钢结构防腐施工技术。 【关键词】：水利工程；钢结构；防腐；施工技术 【 abstract 】 : along with the rapid development of China’s national economy, the state of water conservancy infrastructure investment is constantly increasing, the design of hydraulic structures and scale standards more and more is also high. Steel structures in HanZha engineering application of many, comes, the steel structure of the corrosion problems is more and more outstanding. This article from the steel corrosion principle and equipment protection strategy, the metal thermal spraying technology base and so on water conservancy project introduced steel structure antisepsis construction technology. 【 key words 】 : water conservancy projects; Steel structure; Corrosion; Construction technology 中图分类号：TV文献标识码：A 文章编号： 引言 随着我国国民经济的飞速发展,国家对水利基础建设的投人也不断加大,水工建筑物的设计标准和规模也越来越高。钢结构在涵闸工程中大量运用,随之而来,钢结构的腐蚀问题也越来越突出,钢结构腐蚀给人类带来的损失是很大的。据有关资料统计,世界上每年因腐蚀而报废的金属材料和设备约相当于生产量的20%以上,一些发达国家由于金属腐蚀而造成的经济损失大约占国民经济总产值的2%一4%。钢铁腐蚀后的影响,除了直接损耗以外,从钢结构受力分析,根据日本的统计的资料,在受力情况下钢结构被腐蚀,若腐蚀1%,其强度下降10%一15%;若双面腐蚀各达5%,其结构将报废。随着全球工业的发展,腐蚀的问题日趋严重。就世界范围来说,虽然在污染控制研究的同时,防腐技术措施也在不断发展,使腐蚀问题得到了一些缓解,但总的来说,金属的腐蚀仍十分严重。 水利工程钢结构主要构件是闸门、检修门。由于体积大、吨位重,要求现场安装,甚至现场安装时,防腐也随之在现场进行。下面探讨水工钢结构防腐保护技术。 1、钢设备的腐蚀原理以及防护策略 常温下,钢结构发生腐蚀现象的根本原因是电化学腐蚀,当空气的相对湿度较低时,钢腐蚀发生的几率很小,如果长期相对湿度达到了60%以上,钢腐蚀的程度就会急剧增大,其机理就是电化学反应,整个过程分为以下三步:首先,阳极上的金属失去电子,成为正离子,进入周围环境的溶液中;然后脱离金属束缚的电子从阳极游离到阴极;到达阴极后,电子与阴极的物质发生化学反应,生成相应的还原物,这三个步骤相互联系,如果其中一个过程停止,腐蚀过程也将会终止。 钢结构的腐蚀造成了严重的经济损失,所以,需要预防钢结构腐蚀现象的发生,主要预防措施包括以下几个方面:改善金属结构,在水利工程中,使用防腐性能较好的金属,这种方法需要消耗大量的资金,尤其是大规模的水利工程,具有一定的局限性;在钢结构外部再加一个阴极,从而预防钢结构的腐蚀,这种电化学的防护方法通常用于地下的金属管道以及海边的钢设施;使用缓释剂。在金属表面包上一层有效的防腐材料,比如玻璃钢。e.在金属表面镀上涂层,比如,热镀金属或喷涂金属涂层。热喷涂层是以上五种方法中效果最为显著,因为这种方法操作简单、方便;防腐过程中,产生的副产物较少,对周围的环境几乎没有影响;可以现场施工;涂层不仅起到防腐的作用,还可以加强钢结构的硬度。自从上个世纪五十年代以来,热喷涂层技术在水利工程中,有着广泛的应用,通常情况下,采用锌、铝及其合金热捧涂层的方式,进行钢结构的防护。 2、金属热喷涂的工艺基础 a.金属热喷涂