钢筋混凝土剪力墙施工裂缝研究及控制.doc

钢筋混凝土剪力墙施工裂缝研究及控制【摘要】：钢筋混凝土剪力墙在施工过程中易产生裂缝，其主要的影响因素有：温度应力、原材料质量，地基不均匀沉降，模板支撑不稳，结构配筋，混凝土振捣及养护达不到要求等。文章对钢筋混凝土剪力墙施工中因多种原因造成的非正常裂缝进行了简单分析和说明，在总结目前国内外设计、施工经验以及已有研究成果基础上，提出了钢筋混凝土剪力墙预防裂缝及裂缝处理方法的建议。 【关键词】：钢筋混凝土，剪力墙，施工裂缝，控制 【 abstract 】 : reinforced concrete shear wall cracks in the construction process is easy, the main influence factors are: the temperature stress, raw material quality, the foundation the uneven settlement, templates support instability, structure reinforcement and concrete vibration and maintenance can not reach the requirements, etc. The article to the reinforced concrete shear wall construction for several reasons caused by abnormal fracture of a simple analysis and explain, in both at home and abroad, summarizes the design and construction experience and existing research results are put forward, based on reinforced concrete shear wall to prevent the cracks and crack treatment advice. 【 key words 】 : reinforced concrete, shear wall, construction cracks, control 中图分类号： TU528.571文献标识码：A文章编号： 1 钢筋混凝土剪力墙施工裂缝的成因 钢筋混凝土剪力墙由于组成材料和微观构造的不同以及所受外界影响的不同，产止裂缝的原因较为复杂，它对其结构功能的影晌也是不同的。产生裂缝的原因很多，按其形成的原因可分为两类：一类是由于荷载所引起，如受弯构件、受拉构件等在荷载作用下的混凝土受拉区开裂；另一类是由变形引起的非荷载裂缝，如基础不均匀沉降、温度变化、混凝土的收缩、钢筋锈蚀膨胀等。很多裂缝是多种因素共同作用而形成的。产生裂缝的根本原因是混凝土的抗拉强度太低。 1.1 混凝土水热化引起的裂缝 在大体积混凝土凝结和硬化过程中，水泥和水产生化学反应，释放出大量的热量，称为“水化热”。大部分水化热的热量在浇筑后的前三天释放，由于混凝土不易于导热，因此导致混凝土块体温度升高。当混凝土块体内部的温度与外部环境温度相差很大（一般不宜超过25度），此时形成的温度应力或温度变形逐渐增大，当超过混凝土当时的抗拉强度或极限拉伸值时，就会形成裂缝。 对于钢筋混凝土剪力墙，强度要求较高，水泥用量相对较多，水化热大，温升速率也较大，一般可达35~40℃ ，加上初始温度可使最高温度超过70~80℃。一般混凝土的热膨胀系数为10×-6℃，当温度下降20~25℃时造成的冷缩量为2×10-4~2.5×10-4，而混凝土的极限拉伸值只有1×10-4~1.5×10-4，因而冷缩常引起混凝土开裂。 1.2 塑性收缩裂缝 这种裂缝发生在混凝土浇筑后数小时仍处于塑性状态的时刻。发生这种裂缝的因素是多方面的。大通间的墙面、炎热或大风天气以及混凝土水化热高等，都容易产生这种裂缝。剪力墙一般采用高强混凝土，而高强混凝土的水胶比低．自由水分少，矿物细掺和料对水有更高的敏感性。高强混凝土基本不服水，表面失水更快，塑性收缩比普通混凝土更容易产生，因此相对于普通混凝土构件，剪力墙更容易产生此类裂缝。这类裂缝的宽度可大可小，小的细如发丝，大的可到数毫米，长度可由数厘米到数米，但深度通常不超过5厘米，一般呈现不规则的分布形状。 1.3 塑性塌落引起的裂缝 作为一类大厚度的构件，钢筋混凝土剪力墙在浇筑后的半个小时到数个小时期间，由于混凝土的塑性塌落受到模板或顶部钢筋的制约，或是在在过分凹凸不平的基础上进行浇筑，抑或是模板沉陷